Abstract:Mo–Si–Al–C-based multiphase compounds and their composites reinforced by micro-SiC and TiC particulates were manufactured by means of reactive hot-pressed sintering method. Their microstructure and room temperature mechanical properties were studied. The results showed that Al addition and the ratio of Si/Al exerted a remarkable effect on the reaction products in the Mo–Si–Al–C systems. For the stoichiometric Mo5(Si,Al)3C mixed powders with a molar ratio of Mo:Si:Al:C as 5:1.5:1.5:1, the sintered body contained Mo3Si, Mo3Al2C, and Mo5Si3C as the major reaction products whereas and the minor phases consisted of MoSi2, Mo2C, and Mo(Si,Al)2 compounds. When the starting powder mixture was off-stoichiometric with a small amount of excess Si, only Mo2C accounted for the minor product. Moreover, the relative contents of the former three major phases were affected by the changed Si/Al ratio, where the amounts of Mo3Al2C and Mo5Si3C compounds decreased and increased, respectively with increasing Si/Al ratio. The two multiphase alloys showed poor mechanical properties, due to the existence of residual porosity. In contrast, the composites exhibited superiority in both flexural strength and fracture toughness at room temperature to the Mo–Si–Al–C-based multiphase compounds. MSAC1/20wt.%SiC and MSAC1/20wt.%TiC composites had a respective flexural strength and fracture toughness of 454 and 438MPa, 4.93 and 4.85MPam.

Microstructure and Mechanical Properties of SiC/MoSi_2 Nanocomposites

Microstructure and mechanical properties of SiCp/MoSi2 composites prepared by in situ synthesis and hot-pressing

Microstructures Andmechanical Properties of Hot-Pressed MoSi 2-Matrix Composites Reinforced with SiC and Si 3 N 4 Particles

THE MICROSTRUCTURE AND MECHANICAL PROPERTY OF SiCp/MoSi2 BY IN-SITU REACTION AND HOT PRESS

Microstructure and Mechanical Properties of Sicp/Mosi(2)Composites Manufactured by in Situ Reaction and Hot Pressing

Microstructure,sintering behavior and mechanical properties of SiC/MoSi2 composites by spark plasma sintering

Microstructure and mechanical properties of in situ SiC particulates reinforced MoSi2 matrix composite

Reactive Hot Pressing of SiC/MoSi2 Nanocomposites

MoSi2 Composites Reinforced by SiC Whiskers and Si3N4 Particles

Microstructure and mechanical properties of MoSi2-based composite strengthened and toughened by Si3N4(p) and SiC(w)

Microstructure and Mechanical Properties of Sic/Al Nanocomposite

Microstructures and Mechanical Properties of Hot-Pressed MoSi2–matrix Composites Reinforced with SiC and ZrO2 Particles

Microstructure and Properties of MoSi 2 Intermetallic Reinforced and Toughening by Carbon Nanotube

Processing and Mechanical Properties of Multiphase Composites Based on Mo–Si–Al–C System

Microstructural Characterization of Sintered MoSi<sub>2</sub>/SiC<sub>P</sub> Composites

Si3N4-SiC ceramic nanocomposites

The Microstructure and Mechanical Property of Mo(Si, Al)2-SiC Composite Prepared by Infiltrating Melt Aluminum

Study on the mechanical properties and microstructure of Al2O3/nano-SiC multiphase ceramics

Microstructural characterization of sintered MoSi2/SiCp composites

MoSi2 Inter-Metallic Composites Reinforced and Toughened by CNTs

Synthesis and Mechanical Properties of (mo0.94nb0.06)(si0.97al0.03)2−x Vol% SiC Composites Fabricated Via SHS-HP