Microstructure,sintering behavior and mechanical properties of SiC/MoSi2 composites by spark plasma sintering
HAN Xin-xin,WANG Ya-lei,XIONG Xiang,LI Heng,CHEN Zhao-ke,SUN Wei
DOI: https://doi.org/10.1016/S1003-6326(18)64730-2
IF: 3.752
2018-01-01
Transactions of Nonferrous Metals Society of China
Abstract:SiC/MoSi2composites were synthesized at different temperatures by spark plasma sintering using Mo, Si and SiC powders as raw materials. The phase composition, microstructure and mechanical properties of the as-prepared composites were investigated and the sintering behavior was also discussed. Results show that SiC/MoSi2composites are composed of MoSi2, SiC and trace amount of Mo4.8Si3C0.6phase and exhibit a fine-grain texture. During the synthesis process, there was an evolution from solid phase sintering to liquid phase sintering. When sintered at 1600 ℃, the SiC/MoSi2composites present the most favorable mechanical properties, the Vickers hardness, bending strength and fracture toughness are 13.4 GPa, 674 MPa and 5.1 MPa?m1/2, respectively, higher 44%, 171%, 82% than those of monolithic MoSi2. SiC can withstand the applied stress as hard phase and retard the rapid propagation of cracks as second phase, which are beneficial to the improved mechanical properties of SiC/MoSi2 composites.