Abstract:The impact damage evolution of thermally sprayed WC-Ni coatings was studied under 1-8000 impacts at a fixed load of 10 kN order. With increasing impact number, the accumulative damages of coatings evolve by in-sequence occurrence of WC spallation, coating cracking, and mixed coating/interface cracking accompanied with crack length and width growing. To comprehensively evaluate the coated component performance by observed accumulative damages as the failure criteria, a critical impact number N c with critical load L c is proposed for the onsets of different cracking features. The impact resistance is quantified, by N c ( L cc ) for onset of the coating cracking, and N c ( L cm ) for the mixed coating/interface cracking. A subclassification is identified as N c ( L cm1 ) and N c ( L cm2 ), respectively, for sequential occurrence of the isolated interface cracking and the propagated interface cracking of the penetrated from the coating surface. As the coating thickness is increased from 50 to 200 μm, the impact resistance under a load of 11.1 kN is correspondingly improved with N c ( L cc ) prolonged from 3000 to 4500, and N c ( L cm1 ) from 4500 to 5000. In particular, N c ( L cm2 ) is 6000 for the 50 μm coating, but no N c ( L cm2 ) failure for the 200 μm coating up to 8000 impacts. The impact stress field analysis reveals reduced amplitudes of cyclic surface tensile stress and interface shear stress for the thicker coating, together with the interface shear stress shifting from a tensile-compressive alternating mode to a monotonous tensile one. The impact resistance of coated components under repetitive impacts is interpreted on thermodynamics where the thicker coatings mitigate impact mechanical energy dissipation of plastic strain energy in both coating and steel substrate, and accommodate larger reversible elastic strain energy during the periodic loading-unloading of impact cycles.

Repeated Impact Test for Characterization of Hard Coatings

The Repeated Spherical Indentation Test: an Efficient Way to Evaluate the Adhesion of Hard Coatings

Approach to investigate pre-nucleation fatigue damage of cyclically loaded metals using Vickers microhardness tests

A Method for Evaluating the Impact Wear Behavior of Multilayer TiN/Ti Coating

Thin hard coatings fracture propagation during the impact test

Micro-scale impact resistance of coatings on hardened tool steel and cemented carbide

Evaluation of the Bond Strength of Hard Coatings by the Contact Fatigue Test

Accumulative Damages of Thermally Sprayed Cemented Carbide Coatings Under Repetitive Heavy-Load Impacts

Design for Manufacturing of Cemented Carbide Coated Components Toward High Wear and Impact Resistance Performance

Estimation of fatigue life of TiN coatings using cyclic micro-impact testing

Durability of Plasma-Sprayed Cr 3 C 2 -Nicr Coatings under Rolling Contact Conditions

Damage Analysis Of Tin/Ti Coatings Under Cycling Impact With Hard Particles

Fatigue Resistance and Failure Mechanisms of Plasma-Sprayed CrC–NiCr Cermet Coatings in Rolling Contact

Impact Evaluation Of Plasma Spray Coatings

The Interface Failure Criterion of Coating Materials

Stress-dependent fatigue mechanisms of CrC-NiCr coatings in rolling contact

Evaluation of the Adhesion and Failure Mechanism of the Hard CrN Coatings on Different Substrates

Interfacial fatigue limit as measure of cyclic bonding strength of hard coatings

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Rolling Contact Fatigue Behavior of Plasma-Sprayed CrC–NiCr Cermet Coatings