Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.

Preparation of Activated Carbons from Sawdust by Chemical Activation

Pine Sawdust Derived Ultra-High Specific Surface Area Activated Carbon: Towards High-Performance Hydrogen Storage and Supercapacitors

Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation

PREPARATION OF ACTIVATED CARBON FROM S.ALTERNIFLORA BY H_3PO_4 CHEMICAL ACTIVATION

Mechanism of Biomass Activation and Ammonia Modification for Nitrogen-Doped Porous Carbon Materials.

Preparation and pore characterization of activated carbon from Ma bamboo (Dendrocalamus latiflorus) by H3PO4 chemical activation

Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Hierarchical Pore Structure of Activated Carbon Fabricated by CO2/microwave for Volatile Organic Compounds Adsorption

Preparation of Activated Carbons from Wet Activated Sludge by Direct Chemical Activation.

Physical and chemical properties of carbons synthesized from xylan, cellulose, and Kraft lignin by H3PO4 activation

Physicochemical Properties of Carbons Prepared from Pecan Shell by Phosphoric Acid Activation

Preparation, characterization and adsorption performance of mesoporous activated carbon with acidic groups

Preparation of high mesoporous granular activated carbon with polypropylene and sawdust via dry mix method

Surface Chemistry of Cherry Stone-Derived Activated Carbon Prepared by H3PO4 Activation

INFLUENCE OF DIFFERENT CHEMICAL REAGENTS ON THE PREP-ARATION OF ACTIVATED CARBONS FROM ANTHRACITE

Preparation of High Surface Area Activated Carbons from Luffa Cylindrical Sponge by KOH Activation

Preparation of Biomass Granular Activated Carbon with K2CO3 and Sycamore Tree Sawdust via Dry Mix Process

Methods for preparation and activation of activated carbon: a review

Characterization of activated carbons prepared from sugarcane bagasse by ZnCl2 activation

Preparation of porous carbons from phenol–formaldehyde resins with chemical and physical activation