Abstract:Thermal crosslinking membranes for gas separation have excellent plasticization resistance compared to polymeric membranes. Their low gas permeability, however, is not high enough for industrial application at low cost. In this study, a method, called the sulfonation/desulfonation of the polymeric precursor, was proposed to enhance the CO2 permeability of thermal crosslinking membranes without significantly sacrificing the CO2/CH4 selectivity. The effects of the degree of sulfonation (DS) on the polymeric chain rigidity, interchain distance, and gas separation performance of thermal crosslinking membranes were investigated using dynamic mechanical thermal analysis, a thermal gravimetric analyser coupled with a mass spectrometer, wide-angle X-ray diffraction, and gas permeation tests. Results indicated that the sulfonation/desulfonation of the polymeric precursor significantly influenced the microstructure and gas separation performance of the derived thermal crosslinking membranes. The interchain distance and microvoids of the thermal crosslinking membranes were greatly enlarged by the sulfonation and desulfonation reaction. The rigidity of the polymeric chain was improved by the formation of interchain hydrogen bonding induced by –SO3H groups, which prevent the melting of the polymeric membrane during heat treatment. The gas permeability of the thermal crosslinking membrane was markedly enhanced while the CO2/CH4 selectivity decreased as the DS increased. The CO2 permeability was up to 2.3 times higher than that of the non-sulfonated thermal crosslinking membrane. The separation performance of the derived crosslinking membranes for CO2/CH4 was positioned near or above the 2008 Robeson upper bound.

Influence of heat-treatment on CO2 separation performance of novel fixed carrier composite membranes prepared by interfacial polymerization

Effects of Preparation Parameters on CO2/N-2 Gas Permselectivity of Polyether Thin Film Composite Membrane

Heat treatment for improving performance of inner-side zeolite NaA membranes on composite hollow fibers

Selective Permeation of CO2 Through a Composite Membrane with a Separation Layer of 2-N,n-dimethyl Aminoethyl Methacrylate and Acrylic Acid Copolymer

Preparation of a PVA/Chitosan/Glass Fiber Composite Membrane and the Performance in CO2 Separation

Effect of Process Conditions of Interfacial Polymerization on Performance of Reverse Osmosis Composite Membrane

Effects of Pressure and Temperature on Fixed-Site Carrier Membrane for CO2 Separation from Natural Gas

Thin Zeolite T/Carbon Composite Membranes Supported on the Porous Alumina Tubes for Co2 Separation

Preparation of Polyvinylamine/polysulfone Composite Hollow‐fiber Membranes and Their CO2/CH4 Separation Performance

Fabrication of Sub-Tg Cross-Linked and Thermally Rearranged Poly (Benzoxazole-Co-imide) Hollow Fiber Membrane Derived from Phenolphthalein-Based Copolyimide for CO2/CH4 Separation

Effect of a Heat Pretreatment on the Structure and Properties of Carbon Supports for Carbon Membranes

Preparation of OH/TiO2/PES Composite Membrane by a Novel Gas-Phase Hydrolysis Method in Gas-Liquid Membrane Contactor to Improve the Separation Efficiency of CO2 and CH4

Enhanced CO2 Permeability of Thermal Crosslinking Membrane Via Sulfonation/desulfonation of Phenolphthalein-Based Cardo Poly(arylene Ether Ketone)

Interfacially polymerized polyetheramine thin film composite membranes with PDMS inter-layer for CO2 separation

Preparation and Gas Separation Performance of Composite Carbon Molecular Sieve Membrane from the Polyester Precursor

Study on imidazolium-functionalized polyethersulfone fixed carrier membrane for CO2 separation

Sorption Behavior and Separation Performance of Novel Facilitated Transport Membranes for CO2/CH4 Mixtures

Structural evolution and gas separation properties of thermally rearranged polybenzoxazole (TR-PBO), polymer-carbon transition (PCT) and early-stage carbon (ESC) membranes derived from a 6FDA-hydroxyl-functionalized Tröger's base polyimide

Preparation and Separation Performance of PDMS Composite Membranes for CO2 Separation from CO2-DMC System

Enhanced CO2/CH4 Separation Performance of a Mixed Matrix Membrane Based on Tailored MOF-Polymer Formulations

Thermal Crosslinking of a Novel Membrane Derived from Phenolphthalein-Based Cardo Poly(arylene Ether Ketone) to Enhance CO2/CH4 Separation Performance and Plasticization Resistance