Abstract:This study systematically investigated the influence of (photo-assistance) light exposure on lead zirconate titanate (Pb(ZrxTi1−x)O3, PZT) thin films, with variations of compositions, temperatures and wavelengths of irradiation light. The PZT films were obtained by sol–gel photo-assisted annealing at 150 °C in air atmosphere on Pt coated silicon substrates. They were then baked at 350 °C, and crystallized at 650 °C in air. The physical property analysis results revealed that the UV-photo-assistance affected the microstructure and the texture of the PZT. Furthermore, the influences were strongly dependent on both the film compositions and the wavelengths of the light source. The Fourier transform infrared (FT-IR) spectrometry results showed that the UV-light enhanced the decomposition process within the solution layer and dissociated the organic species during drying at 150 °C, and the observed structural variation of the PZT films was closely associated with the residual amount of their organics after photo-assisted annealing. The UV-absorption spectra of PZT precursors indicated that the enhancement of the organic decomposition was dependent on their photo-sensitivities, which were determined by the compositions and temperatures. Additionally, the analyses of various photo-assistances conducted on the sol–gel solution provided specific information about the interaction between the photo-lights and the solution precursors. The results suggest a preferential decomposition of Ti oligomers during the photochemical annealing process, which is considered as the most important mechanism for structural variations in the photo-assisted PZT film. This study proposed that PZT has a novel texture development mechanism under UV radiation, namely, the photochemical-induced-self-seeding effect. Based on this mechanism, it has become feasible to manipulate the texture of the multi-component materials through the photochemical deposition process.

Enhancement of Photovoltaic Effect of PLZT Ceramics by Compositional Optimization and Grain Size Control

Compositional effect on piezoelectric and anomalous photovoltaic properties of PLZT ceramics with fixed grain sizes

Ferroelectric and Photostrictive Properties of Fine‐Grained PLZT Ceramics Derived from Mechanical Alloying

Photostriction Properties of PLZT (4/52/48) Ceramics Sintered by SPS

Effects of Preparation Conditions on the Structural and Optical Properties of Spark Plasma‐Sintered PLZT (8/65/35) Ceramics

Photostrictive Mathematical Model Of Plzt Ceramics: Constitutive Modeling And Experimental Validation

Microstructures and Pyroelectric Properties of Multicomposition 0.9PbZrO<sub>3</sub>·<i>x</i>PbTiO<sub>3</sub>·(0.1−<i>x</i>)Pb(Zn<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub>Ceramics

Microstructures And Pyroelectric Properties Of Multicomposition 0.9pbzro(3)Center Dot Xpbtio(3)Center Dot(0.1-X)Pb(Zn1/3nb2/3)O-3 Ceramics

Controllable Photoinduced Scattering and Optimized Light Emission Intensity in Nd3+ Doped (pb, La)(Zr, Ti)O-3 Perovskite Ceramics

Mechanism Of Photochromic Effect In Pb(Zr,Ti)O-3 And (Pb,La)(Zr,Ti)O-3 Ceramics Under Violet/Infrared Light Illumination

Diffusion in Multi-Compositional Pz-Pt-Pzn Ceramics Prepared by Spark Plasma Sintering

ELECTRON-MICROSCOPY STUDIES OF PURE AND DOPED ELECTROOPTIC PLZT CERAMICS

Photochemical-induced self-seeding effect on lead zirconate titanate thin film

Microstructure and Electrical Properties of PLZT Ceramics from Pb3O4 As the Lead Source

Intrinsic and Extrinsic Size Effects in Fine-Grained Morphotropic-Phase-Boundary Lead Zirconate Titanate Ceramics

A Novel Approach to Improving the Electromechanical Properties of PZT-based Piezoelectric Ceramics Via a Grain Coating Modification Strategy

Effect of Zr:Sn ratio in the lead lanthanum zirconate stannate titanate ceramics on microstructure and electric properties

Strain Characteristics of PLZT-Based Ceramics for Actuator Applications

Microstructure and dielectric properties of PLZST ceramics prepared by a modified coprecipitation

Processing and characterization of lead zirconate titanate nanopowders by a simple water-based sol-gel method

Energy storage properties of PLZST ceramics with tetragonal/orthorhombic two-phase coexistence