The Influences of Monovalent Ions on the Stability of Scintillation Properties and Radiation Hardness of PbWO4:Y3+ Crystals
X Zhang,JY Liao,PJ Li,JJ Xie,BF Sheng,PF Shao,ZW Yin
DOI: https://doi.org/10.1016/s0168-9002(02)00863-x
2002-01-01
Abstract:Some Y3+-doped PbWO4 crystals grown by modified Bridgmann method showed exceptional behaviors, namely, light yield increased after low dose rate irradiation, and the radiation-induced absorption coefficient was negative around 430nm. In this paper, the influences of monovalent ion impurities (Na+ and K+) on the stability of scintillation properties and radiation hardness were studied. The experimental results show that Na+ ion enhances the absorption band at cut-off edge and at 430nm, while K+ ion only makes optical transmission unstable around 430nm when the crystals were annealed at high temperatures. The contamination by Na+ and K+ ions makes scintillation properties and radiation hardness more unstable in the temperature range from 50°C to 350°C. The radiation-induced absorption coefficient is also negative around 430nm. The charge compensation mode of K+ ion along the crystal does not change, but those of Na+ ion are different along the crystal. The concentrated Na+, K+ and Y3+ ions, which occupied Pb sublattice, lead to the shortage of Pb vacancies (VPb″). Thus instead of the formation of [2(Y3+Pb)—VPb″] ((Y3+Pb) stands for the Y3+ ion occupying the Pb sublattice), Na+ and K+ ions compel the defect (Y3+Pb) to form cluster [2(Y3+Pb)—Oi″] or [(Y3+Pb)—Oi″+hole] in which the interstitial oxygen (Oi″) was considered to be the origin of light yield increase after low dose rate irradiation.