Abstract:FePt films were deposited on Cr 1-x Mo x underlayers by dc magnetron sputtering. The effects of the Mo content in the underlayers, underlayer thickness, substrate temperature, and FePt film thickness on the structural and magnetic properties of the FePt films were studied. Experimental results showed that the (200) textured Cr 90 Mo 10 film was a promising underlayer for promoting the growth of the L1 0 FePt films with (001) preferred orientation at relatively low temperatures. With the Cr 90 Mo 10 underlayers, the ordering process of the FePt films could start at 200 °C. Both the ordering degree and the out-of-plane coercivity (H c ) of the FePt films increased with an increase in substrate temperature. When the substrate temperature was ≥250 °C, the FePt films grown on the Cr 90 Mo 10 underlayers could have the (001) preferred orientation. The FePt films grown on the Cr 90 Mo 10 underlayers at different temperatures showed a continuous microstructure. The out-of-plane coercivities H c decreased while the ordering degree increased with increased FePt film thickness, which could be due to the variation of the magnetic reversal mechanism from rotation predominant mode to domain wall motion predominant mode.

Formation of (001) Texture in Fe-O Underlayered L1(0) Fept Films

Formation of (002) texture in Fe films prepared by thermal treatment

Formation of (0 0 2) texture in Fe films prepared by thermal treatment

SiO2 layer thickness effects on the (001) texture of FePtCu:SiO2 nanocomposite films

Structural and Magnetic Properties of FePt Films Grown on Cr1-xMox Underlayers

Origin of (0 0 1) Orientation and Superlattice Structure Identification in L10-FePt/B4C Multilayer Thin Films

Improvement of Magnetic Property of L1-FePt Film by FePt∕Au Multilayer Structure

Structural and magnetic properties of FePt films grown on Cr 1-x Mo x underlayers

Preparation of (001) oriented L10 phase FePt thin films by alternate sputtering

The Mechanism of Texture Evolution in Annealed L10–FePt Thin Films

Effects of Substrate on Structure and the Magnetic Properties of (001)-Textured FePt Films Grown at Low Temperature

Microstructural and magnetic properties of L1 0 FePt C (0 0 1) textured nanocomposite films grown on different intermediate layers

Orientation Control in L10 FePt Films by Using Magnetic Field Annealing Around Curie Temperature

Growth and Magnetism of Ultrathin Fe Films on Pt(100)

Effect of Annealing on the Microstructures and the Magnetic Properties of [fe/pt]16 Multilayers on MgO (001) Substrates

Microstructural and magnetic properties of L1<sub>0</sub>FePt–C (0 0 1) textured nanocomposite films grown on different intermediate layers

Structure and magnetic properties of FePt/Au multilayer film

Enhanced Structural And Magnetic Ordering Of Fept/Mn-Oxide Bilayers By Ion-Beam Bombardment And Annealing

Low Temperature Ordering of FePt Films by In-Situ Heating Deposition Plus Post Deposition Annealing

Microstructure and magnetic properties of FePt thin films for the coating of magnetic force microscopy tips

Enhancement of Magnetic Anisotropy for L10-(0 0 1) FePt Films Grown on SrTiO3 Substrate