Effect of denucleating glass composition on undercooling of Fe83Ga17 alloy melts

Jiankun Zhou,Jianguo Li

DOI: https://doi.org/10.1016/j.jallcom.2007.11.145

IF: 6.2

2009-01-01

Journal of Alloys and Compounds

Abstract:Adopting glass fluxing combined with superheating cycling method, the undercooling and its stability of Fe83Ga17 alloy melts were investigated using different kinds of denucleating glass: B2O3, 90% NaSiCa+10% B2O3 (simplified as Na–Si–Ca–Al–B) and 70% Na–Si–Ca–Al–B+30% Na2B7O4. The results showed that different glass has different denucleating mechanism. The purification of B2O3 glass is only a physical process, by which the stable bulk undercooling cannot be obtained during superheating–cooling cycles. While taking Na–Si–Ca–Al–B glass as purifying agent, its denucleating mechanism is a comprehensively physicochemical process. But the stability of undercooling is still undesirable because of the separation between melt and glass during cooling process in superheating cycling. A stable bulk undercooling can be obtained by physicochemical denucleating process in the case of 70% Na–Si–Ca–Al–B+30% Na2B7O4 molten glass owing to its suitable viscosity.