The effects of microstructure, Nb content and secondary Ruddlesden-Popper phase on thermoelectric properties in perovskite CaMn1- x Nb x O3 (x = 0-0.10) thin films
E Ekström,A le Febvrier,F Bourgeois,B Lundqvist,J Palisaitis,P O Å Persson,O Caballero-Calero,M S Martín-González,J Klarbring,S I Simak,F Eriksson,B Paul,P Eklund
DOI: https://doi.org/10.1039/c9ra10007e
2020-02-24
Abstract:CaMn1-x Nb x O3 (x = 0, 0.5, 0.6, 0.7 and 0.10) thin films have been grown by a two-step sputtering/annealing method. First, rock-salt-structured (Ca,Mn1-x ,Nb x )O thin films were deposited on 11̄00 sapphire using reactive RF magnetron co-sputtering from elemental targets of Ca, Mn and Nb. The CaMn1-x Nb x O3 films were then obtained by thermally induced phase transformation from rock-salt-structured (Ca,Mn1-x Nb x )O to orthorhombic during post-deposition annealing at 700 °C for 3 h in oxygen flow. The X-ray diffraction patterns of pure CaMnO3 showed mixed orientation, while Nb-containing films were epitaxially grown in [101] out of-plane-direction. Scanning transmission electron microscopy showed a Ruddlesden-Popper (R-P) secondary phase in the films, which results in reduction of the electrical and thermal conductivity of CaMn1-x Nb x O3. The electrical resistivity and Seebeck coefficient of the pure CaMnO3 film were measured to 2.7 Ω cm and -270 μV K-1 at room temperature, respectively. The electrical resistivity and Seebeck coefficient were reduced by alloying with Nb and was measured to 0.09 Ω cm and -145 μV K-1 for x = 0.05. Yielding a power factor of 21.5 μW K-2 m-1 near room temperature, nearly eight times higher than for pure CaMnO3 (2.8 μW K-2 m-1). The power factors for alloyed samples are low compared to other studies on phase-pure material. This is due to high electrical resistivity originating from the secondary R-P phase. The thermal conductivity of the CaMn1-x Nb x O3 films is low for all samples and is the lowest for x = 0.07 and 0.10, determined to 1.6 W m-1 K-1. The low thermal conductivity is attributed to grain boundary scattering and the secondary R-P phase.