Abstract:A nanostructure of lithium-zinc copper ferrite (LiZnCu-Ferrite) prepared experimentally by the auto-combustion method depends on different parameters. The auto-combustion method operates at a temperature (160 °C) suitable for preparing the required nanostructure ferrite phase. The dependent composition was [Li0.5-xZnxCuxFe2.5-xO4 at (x = 0, 0.05, 0.15, 0.25, 0.35, and 0.45)]. A pre-firing at temperature (650 °C) was applied during the calcination process that was suitable to remove unwanted products. The sintering at temperature (800 °C) was suitable for a pelletized shape of ferrite samples. The X-ray diffraction (XRD) pattern showed a spinel structure of ferrite phase produced for all samples under study with the lattice constant in the range (8.345–8.368 Å) as a function of (x). The crystallite size was in the range (18.41–30.27 nm) calculated by the Scherrer method. The transmission electron microscope (TEM) showed a production of nanorods in the size range (10–45 nm) and nanoparticles in the size range (10–40 nm). There was a coincidence between the results of the XRD and TEM analyses. On the other hand, the scanning electron microscope (SEM) showed the surface morphology and the nature of grain size, which was a sign of the presence of nanostructure; it agreed with the XRD analysis. FTIR spectra showed evidence that the system Li0.5-xZnxCuxFe2.5-xO4 had spinal ferrite nanoparticles successfully prepared by sol-gel auto-combustion. A vibrating sample magnetometer (VSM) showed a change in magnetic parameters as compensation factor (x) increased for all composites of LiZnCu-ferrite such as saturation magnetization (Ms), initial magnetic permeability (μi), remanence (Mr), and coercive force (Hc) that measured from M − H loops. A saturation magnetization increased as a function of (x) and recorded a maximum value at (x = 0.15). While the coercivity, initial magnetic permeability (μi), and remanence magnetization enhanced as a function of (x) and recorded a maximum value at (x = 0.45).

Preparation and Magnetic Properties of Y-Type Ferroxplana by Sol-Gel Method

Preparation and Magnetic Properties of Zn–Cu–Cr–Sm Ferrite Via a Rheological Phase Reaction Method

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Preparation and Magnetic Properties of ZnCuCrLa Ferrite and Its Nanocomposites with Polyaniline

Phase formation process, microstructure and magnetic properties of Y-type hexagonal ferrite prepared by citrate sol–gel auto-combustion method

Preparation and Magnetic Characterization of the Ferroxplana Ferrites Ba3Co2−xZnxFe24O41

Structural and Magnetic Characteristics of Ferroxplana Co2Y Nanoferrites Synthesized via Two Chemical Routes

Magnetic Properties of Non-Stoichiometric Y-Type Hexaferrite

Preparation and Magnetic Characterization of Y-Type Hexaferrites Containing Zinc, Cobalt-And Copper

Preparation of the Percolative Nickel-Zinc Ferrite/Barium Titanate Composite Ceramics with Liquid-Solid Hybrid Method

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

The Physic Properties of Bi–Zn Codoped Y-type Hexagonal Ferrite

Magnetic structure and colossal dielectric properties in Ga 3+ substituted Zn 2 Y hexaferrites by chemical co-precipitation method

Preparation and magnetic properties of titanium-substituted LiZn ferrites via a sol-gel auto-combustion process

Electromagnetic Properties Of Mn-Doped Nicuzn Ferrites Prepared By Sol-Gel Auto-Combustion

Structure phase transition and magnetic properties of nanocrystalline

Effect of Substitution on Magnetization Mechanism for Y-type Hexagonal Ferrite

Effects of Mno2 on the Electromagnetic Properties of Nicuzn Ferrites Prepared by Sol-Gel Auto-Combustion

Sol gel auto combustion method to prepare nanostructures LiZnCu ferrite

Preparation and Magnetic Properties of BaZn2−xCoxFe16O27 Nanocrystalline Powders by the Stearic Acid Gel Method

Cr3+ doping-controlled magnetic and dielectric properties of polycrystalline Y-type BaSrCo2Fe11-xCrxAlO22 hexaferrite