Abstract:Hollow fiber membranes fabricated via dry/wet phase inversion method usually have two dense skin layers,which will increase its resistance of mass transport as a support membrane. It is necessary that the dense skin layer of support membrane has been eliminated to improve separation performance of composite membrane. The excellent. chemical resistance of poly(vinylidene fluoride) (PVDF) to many acids and alkalis has made it as an attractive membrane material, and then it's often fabricated as porous hollow fiber membrane by phase inversion. In the process, the formation of the skin layer is due to the rapid exchange between solvent and coagulation, so many attempts have been made to slow it, so as to control the formation of the skin layer. In this paper, it has been found that the fabrication progress becomes unstable, and the membrane prepared has noncircular lumen, when the "weak" or "soft" coagulation is used. To increase the fabrication solution stability during membrane formation, dope viscosity was focused in this experiment. Dimethyl acetamide (DMAc) was used as solvent as well as internal coagulant, and the additives including LiCl, water and surfactant Span were chosen to investigate their effect oil the viscosity of the fabrication solution. The dope viscosity will greatly increase after adding LiCl, while the variety of dope viscosity is unconcerned in the fabrication solution concentration as adding water. The homogenization and stability of the fabrication solution are improved by adding Span,and the viscosity increases at the same time. Without increasing PVDF concentration, the stability of the nascent membrane was improved by increasing the fabrication viscosity. The PVDF hollow fiber membrane with the structure of single outer skin layer and finger-like pore through the cross-section, has been successfully fabricated. The mean pore radius and water flux of the single skin hollow fiber membrane were greatly improved.

Effects of Molecular Weight of Polyvinylpyrrolidone on Precipitation Kinetics During the Formation of Asymmetric Polyacrylonitrile Membrane

Effects of Preparing Condition on PVDF Membrane Morphology

The Polymer-rich Phase Solidification Process of PVDF-PVP-DMAc-H2O Solution

Influence of additives on phase separation process of PVDF solution and membrane morphology

Effect of Polymer Molecular Weight on the Morphology and Crystallization of Prepared PVDF Membranes

Effect of the Permeants/Polymer Interactions on the Pervaporative Separation Properties of the P(Vdf-Co-Hfp) Membrane

Leaching of PVP from Polyacrylonitrile/pvp Blending Membranes: A Comparative Study of Asymmetric and Dense Membranes

Effect of the Casting Solvent on the Crystal Characteristics and Pervaporative Separation Performances of P(Vdf-Co-Hfp) Membranes

Effect of Additives on the Morphology and Performance of Symmetric Network PVDF Membranes

INFLUENCE OF ALCOHOL-BASED NONSOLVENTS ON THE FORMATION AND MORPHOLOGY OF PVDF MEMBRANES IN PHASE INVERSION PROCESS

Effect of Polyvinylpyrrolidone Molecular Weights on Morphology, Oil/Water Separation, Mechanical and Thermal Properties of Polyetherimide/Polyvinylpyrrolidone Hollow Fiber Membranes

Preparation of Symmetric Network PVDF Membranes for Protein Adsorption Via Vapor-Induced Phase Separation

Morphology and Formation Mechanism of Poly(Vinylidene Fluoride) Membranes Prepared with Immerse Precipitation: Effect of Dissolving Temperature

Effect of Polymer Additives PVP and PEG on the Diffusion Property of PVDF/PVP(PEG)/DMAc Dope Solution

Effect of Dissolving Temperature of Dopes on the Morphology of PVDF Membrane

Influence of Dope Viscosity on the Fabrication of Pvdf Hollow Fiber Membranes with Single Skin Layer

Influences of adding organic intermediate layer on membrane formation and properties

Effect of Maturation Time of Dopes on the Morphology and Crystallization of PVDF Membranes

Effect of Coagulant on the Coagulation Kinetics and Membrane Properties of PVA-PEG-H2O System

Preparation of poly (vinyl butyral) hollow fiber ultrafiltration membrane via wet-spinning method using PVP as additive

PVDF Membrane Morphology—Influence of Polymer Molecular Weight and Preparation Temperature