Abstract:In the present work, high-quality MgSiN2 powders were prepared by a combustion synthesis method, based on Mg-Si3N4-N-2 system. The effects of additive content (NH4Cl or NH4F) and N-2 pressure on phase composition and crystal morphology of products were investigated. The results suggested that both NH4Cl and NH4F additives alleviated agglomeration and decreased the grain size of MgSiN2. In addition, NH4Cl did not result in the formation of an extra impurity, while MgF2 residue was found when NH4F was introduced. Therefore, NH4Cl additive was considered as a better choice for the preparation of MgSiN2 powders in comparison with NH4F additive. According to the observation of some MgSiN2 whiskers and notably increased Si content under low N-2 pressure, the pressure of N-2 over 0.5 MPa was essential to have a complete reaction in the present work. Finally, MgSiN2-Si3N4 composite powders with quasi-spherical morphology were prepared by adding excessive Si3N4 and NH4Cl additive in reactant. The formation and growth mechanism of MgSiN2 grains was reasonably speculated based on the experimental results. Because of the remarkable merits, the as-prepared Si3N4-MgSiN2 composite powders showed great potential for alternative sintering aid in the sintering of Si3N4-based ceramics.

Synthesis of MgSiN2 Cuboids by a Solid-state Reaction

Large-scale synthesis of magnenium silicon nitride powders at low temperature

Low‐Temperature Synthesis of Nanocrystalline Α‐si3n4 Powders by the Reaction of Mg2Si with NH4Cl

Solid State Synthesis of Nitride, Carbide and Boride Nanocrystals in an Autoclave

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Low-Temperature Synthesis of Nanocrystalline α-Si<sub>3</sub>N<sub>4</sub>Powders by the Reaction of Mg<sub>2</sub>Si with NH<sub>4</sub>Cl

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

The Role of MgSiN2 During the Sintering Process of Silicon Nitride Ceramic

Vapor-Solid Reaction for Silicon Carbide Hollow Spherical Nanocrystals

Low Temperature Solid-State Synthesis of Nanocrystalline Gallium Nitride

Synthesis of Spherical Si3N4 Powders by Liquid‐phase Modified Carbothermal Reduction and Nitridation

Solid State Synthesis of a New Ternary Nitride MgMoN2 Nanosheets and Micromeshes

Additive-Assisted Nitridation to Synthesize Si<sub>3</sub>N<sub>4</sub>Nanomaterials at a Low Temperature

Synthesis and Growth Mechanism of Single Crystal Β‐si3n4 Particles with a Quasi‐spherical Morphology

Nitridation of Silica to an Α‐silicon Nitride Nanorod Using NaNH2 in the Autoclave at 700°C

Additive‐Assisted Nitridation to Synthesize Si3N4 Nanomaterials at a Low Temperature

NbN and NaNbN2 Particles: Selective Solid State Synthesis and Conduction Performance.

Synthesis and Characteristics of Cubic Silicon Carbide Nanospheres with Smooth Surfaces.

Sulfur-assisted synthesis of nitride nanocrystals.

In-Situ Reactive Synthesis of AlN-SiC Composites and Solid Solutions

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction