Abstract:Several nanostructures were obtained after irradiation with femtosecond laser pulse (130fs, 800nm, 1kHz pulse repetition frequency) on Au/Cr film stack. The influence of laser parameters such as fluence (0.5J/cm2, 1.5J/cm2, 3J/cm2) and the number of pulse were investigated. With single pulse irradiation, the nanoline and nonoparticle were obtained for the pulse fluence of 0.5J/cm2 and 3J/cm2, respectively. The formation mechanism of those nanostructures was discussed. The results of this experiment demonstrate that different kinds of nanostructures could be formed by varying the laser parameters such as fluence and the number of pulse.

Variety of Nanostructures Induced by Femtosecond Laser Pulses on Surface of Au/Cr Film Stack