Abstract:The laser ablation of aluminum alloy 6061 was studied both experimentally and by computational modeling in this work. Six variations of the number of pulses of irradiation (1, 5, 10, 20, 50, and 100 pulses) combined with four different laser fluence (2.0 J/cm2, 1.5 J/cm2, 1.0 J/cm2, and 0.5 J/cm2) were chosen to study the effect of heat input and laser action time on microstructural changes and the generation of particulate pollutants. Laser fluence and the number of pulses of laser irradiation were found to have a direct influence on thermal diffusion and the ablation depth of aluminum alloy 6061. At a relatively high laser fluence (2 J/cm2) and with the application of 10 pulses of irradiation, ablation cracks were observed on the surface of aluminum alloy 6061 and the production of pollutant particles increased according to a particle counter. Maintaining the laser fluence at 0.5 J/cm2 while increasing the number of pulses of irradiation to 50 also enhanced the depth of thermal diffusion while laser ablation continued to occur. The occurrence of vaporization in the surface region was influenced largely by laser fluence and the number of pulses of irradiation, as evident from the simulation and from experimental results. The single laser pulse duration was 6 ns and the repetition rate was 1 s−1. This article provides a novelty numerical model which could reveal the metal alloys' evapotation at a high-fluence nanosecond laser ablation. A 3D computational model was used to predict the temperature variation upon laser irradiation in a solid material over time. The results of the model (thermal diffusion versus laser ablation) agreed well with the experimental results.

Nanoscale surface modifications and formation of conical structures at aluminum surface induced by single shot exposure of soft x-ray laser pulse

(Sub-)picosecond surface correlations of femtosecond laser excited Al-coated multilayers observed by grazing-incidence x-ray scattering

Single-shot femtosecond laser processing of Al-alloy surface: An interplay between Mbar shock waves, enhanced microhardness, residual stresses, and chemical modification

Sub-nanometer scale depth patterning on sapphire crystal by femtosecond soft x-ray laser pulse irradiation

Nanoscale subsurface dynamics of solids upon high-intensity laser irradiation observed by femtosecond grazing-incidence x-ray scattering

Delayed onset and directionality of x-ray-induced atomic displacements observed on subatomic length scales

Laser Fabrication of Nanostructures on a Pure Aluminum Surface in Air

Formation of nano-sized films on the surface of pure Al by Nd: YAG pulsed laser irradiation

Effects of Laser Fluence on Near-Field Surface Nanostructuring

Variety of Nanostructures Induced by Femtosecond Laser Pulses on Surface of Au/Cr Film Stack

Subsurface hardening of Al irradiated with ultrafast infrared laser

Microstructure Formations Resulting from Nanosecond and Picosecond Laser Irradiation of a Ti-Based Alloy under Controlled Atmospheric Conditions and Optimization of the Irradiation Process

Numerical and Experimental Investigation on Pulsed Nanosecond Laser Ablation Processing of Aluminum Alloy

Surface Nanostructuring by Nano-/Femtosecond Laser-Assisted Scanning Force Microscopy

Sub-Wavelength Surface Structuring of Niti Alloy by Femtosecond Laser Pulses

Extending Femtosecond Laser Fabrication of Micro- and Nanoscale Structures from A Planar to Non-Planar Metal Surface

Structure Formation on the Surface of Alloys Irradiated by Femtosecond Laser Pulses

Investigating and understanding the effects of multiple femtosecond laser scans on the surface topography of metallic specimens

Formation of high-aspect-ratio nanocavity in LiF crystal using a femtosecond of x-ray FEL pulse

Femtosecond laser induced surface structures on amorphous alloys

Mechanism of Femtosecond-Laser-induced Periodic Nanostructure Formation on Crystalline Silicon Surface Immersed in Water