Effect of pH and current density on the physical properties of cobalt obtained by electrowinning from sulfate solutions
Fabiano Augusto Costa Mafra Passos,Jonas da Cruz Trajano de Souza,Iranildes Daniel dos Santos,Reiner Neumann,Pedro Paulo Medeiros Ribeiro,Achilles Junqueira Bourdot Dutra
DOI: https://doi.org/10.1016/j.mineng.2024.108697
IF: 5.479
2024-04-16
Minerals Engineering
Abstract:Cobalt is a critical metal, essential for the advancement of modern society, due to its applications on technology, energy and chemical industries. The primary aim of this paper was investigating, through voltammetric and bench scale electowinning tests from acidic cobalt sulfate solutions under typical industrial operational conditions, the effects of electrolyte pH and current density on parameters such as current efficiency (CE), specific energy consumption (SEC), morphology, structure and physical properties of the metallic cobalt deposit. The cobalt electrodeposits were characterized by X-ray diffraction (XRD), scanning electron microscopy coupled with energy dispersive spectrometry (SEM/EDS) and Vickers microhardness measurements. Results indicated that the deposition mechanisms, which are pH dependent, play an important role on the investigated parameters. A remarkable effect of both current density and electrolyte pH was observed. The highest CE, 95.5 %, was achieved with a current density of 400 A/m 2 at pH 4.0, while the lowest SEC, 1.93 kWh/kg, was obtained with 200 A/m 2 at pH 3.0. Brighter and smoother deposits were obtained in tests at pH 5.0. The presence of the FCC-Co phase was only identified in the deposits obtained at pH 4.0, while at pH 3.0 and 5.0 only HCP-Co phase was observed, with differences in preferential crystallographic orientation. Tests with 400 A/m 2 at pH 5.0 rendered the largest average crystallite and grain sizes (CS and GS, respectively), 68.8 nm and 33.0 μm respectively, whose microhardness (MH) was 169.8 HV, with a CE of 94.4 % and a SEC of 2.41 kWh/kg. The smallest CS and GS were obtained in the tests with current density of 400 A/m 2 at pH 3.0, 11.9 nm and 1.8 μm respectively, rendering a MH value of 309.2 HV. Considering all the variables involved, the more attractive electrowinning conditions should be at pH 5.0 and 400 A/m 2 , as they led to a smoother and more ductile deposit, despite the slightly higher SEC (2.41 kWh/kg).
engineering, chemical,mining & mineral processing,mineralogy