A new Co-doped PbO 2 anode for copper electrowinning: Electrochemical and morphological characterization

R. Rezaei,K. Jafarzadeh,S.M. Mirali,H. Mazhari Abbasi

DOI: https://doi.org/10.1016/j.est.2024.111053

IF: 9.4

2024-02-28

Journal of Energy Storage

Abstract:Anodic electrodeposition was used to create a high catalytic activity Co-doped PbO 2 composite coating on Ti substrate, in order to reduce the overpotential and raising the electrocatalytic activity for oxygen evolution during the copper electrowinning process. The temperature, composition, and current density of the electrolyte were investigated in order to produce a composite anode with the best electrocatalytic behavior, stability, and efficiency in the electrowinning process. Scanning electron microscopy (SEM) was utilized to investigate the morphology of the coating, and electrowinning, cyclic voltammetry (CV), and the accelerated life time test (ALT) were employed to evaluate the electrodes' electrochemical behavior. The ideal conditions in this investigation involved 65 g.L −1 cobalt nitrate with a 5 mA.cm −2 current density at 65 °C for the electrodeposition of Co-doped PbO 2 coating. Furthermore, the potential for oxygen evolution of the PbO 2 -CoO x anode was found to be approximately 180 and 220 mV lower than that of the PbO 2 and Pb-Ca-Sn anodes, respectively, based on the results of the electrochemical test. The ALT test results showed that the PbO 2 -CoO x anode had a significantly lower initial cell voltage than the Pb-Ca-Sn and PbO 2 anodes; however, this value increased after 165 h due to the anode's mechanical breakdown. The results showed that Cu electrowinning efficiency for Pb-Ca-Sn, PbO 2 , and PbO 2 -CoO x was 91.9 %, 98.4 %, and 100 % respectively.

energy & fuels