Strain Rate Sensitivity of Tensile Properties in Ti–47Al–2Mn–2Nb–0.8TiB2 Alloy

Y Wang,DL Lin,YX Zhou,YM Xia,CC Law

DOI: https://doi.org/10.1016/s0167-577x(99)00064-6

IF: 3

1999-01-01

Materials Letters

Abstract:Strain rate sensitivity of tensile properties of Ti–47Al–2Mn–2Nb–0.8TiB2 alloy with near lamellar (NL) microstructure were investigated within a strain rate range from 10−5 s−1 to 103 s−1 using conventional static tensile testing technique, and a self-designed Split–Hopkinson tensile bar set-up with a rotating disk. Corresponding fracture surfaces at different strain rates were analyzed using a scanning electron microscope. It was found that tensile ductility fluctuates within a narrow range with the variation of the strain rate: dynamic elongation approximates to static elongation. But dynamic strengths σd of the alloy are obviously higher than static strengths σs; there exists a linear relationship between σs and the logarithm of the strain rate (σs=A+Bln ε̇), but between dynamic strength σd and the strain rate (σd=C+Dε̇). Fractography analysis indicates that the alloy fractures in a mixed mode of predominant transgranular cleavage and minor intergranular cracking under static and dynamic strain rates. Environmental effect is excluded from a main cause for the room-temperature brittleness of the investigated alloy.