Abstract:In this research, the microstructure evolution, mechanical properties, and creep mechanisms of Mg-12Gd-1MM-0.6Zr (wt%) alloy under different conditions were systematically studied using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and tensile creep tests. Regarding the microstructure of the as-cast sample, the average grain size was about 42 μm, and the eutectic compounds were determined to be Mg5(Gd0.8MM0.2). During homogenization, these eutectic compounds gradually dissolved, and Mg12MM particles were precipitated. During hot extrusion, complete dynamic recrystallization (DRX) occurred, resulting in equiaxial grains with an average grain size of about 12 μm and the formation of streamlines consisting of Mg12MM particles along the extrusion direction (ED). After T5 treatment (225 °C for 7 h), a large number of β'(Mg7Gd) phases were precipitated on the {11-20}α habit plane and were interconnected, forming an interlaced network structure. The ultimate tensile strength (Rm = 405 MPa) and yield strength (RP0.2 = 288 MPa) of the T5 sample were significantly higher than those of the as-extruded sample (Rm = 289 MPa, RP0.2 = 185 MPa), but the elongation (A = 4%) was remarkably lower than that of the as-extruded sample (A = 18%). When crept at 225 °C under 100 MPa, the steady-state creep rates of the as-cast, as-extruded, and T5 samples were 1.59×10–8, 1.08×10–8, and 1.40×10–8 s–1, respectively, and their total strains within 100 h were respectively breaking, 0.81%, and 0.92%, indicating that the as-extruded alloy exhibited the best creep resistance. TEM analysis revealed that, during the creep process of the T5 sample, the β' particles coarsened and the precipitate-free zones (PFZs) widened, which increased the steady-state creep rate and the total strain within 100 h as compared with the as-extruded sample.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S100207212100020X-fx1_lrg.jpg">Download : Download high-res image (126KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S100207212100020X-fx1.jpg">Download : Download full-size image</a></li></ol>

Microstructure and Creep Behavior of the Extruded Mg–4Y–4Sm–0.5Zr Alloy

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Compressive creep behavior of extruded Mg-4Sm-2Yb-0.6Zn-0.4Zr alloy

Creep Behaviors and Microstructure Evolution of Mg-5Y-2Nd-3Sm-0.5Zr Alloys

Tensile Creep Behavior and Microstructure Evolution of Mg-11Gd-2Y-0.5Zr Alloy

Influence of Extrusion Temperature on Microstructure and Mechanical Properties of Mg-4Y-4Sm-0.5Zr Alloy

Influence of Thermal and Thermo-Mechanical Processing on the Creep Resistance of Mg-10Gd-3Y-0,4Zr Alloy

Microstructure Evolution and Creep Behavior of High-Pressure Die-Cast Mg–9Al–1Zn–1Sr Alloy

Abnormal creep behavior of Mg-12Gd-1MM-0.6Zr (wt.%) alloy at 300C

Creep Deformation Mechanism and Microstructure Evolution of Mg-3Sm-0.5Zn-0.4Zr Alloy

Creep Behavior of Mg–11Y–5Gd–2Zn–0.5Zr (wt.%) at 573 K

Abnormal creep behavior of Mg–12Gd–1MM–0.6Zr (wt.%) alloy at 300°C

The Impression Creep Behavior and Microstructure Evolution of Cast and Cast-then-extruded Mg–10Gd–3Y–0.5Zr (Wt%)

Microstructural evolution of Mg–14Gd–0.4Zr alloy during compressive creep

High Temperature Compressive Deformation Behavior of an Extruded Mg–8Gd–3Y–0.5Zr (wt.%) Alloy

Microstructure evolution, mechanical properties and creep mechanisms of Mg-12Gd-1MM-0.6Zr (wt%) magnesium alloy

Tensile creep behaviors of Mg-10Gd-0.4Zr alloy in different heat treatment states

Mechanical Properties and Creep Behavior of Mg-Gd-Y-Zr Alloys

Study on the microstructures and tensile creep behaviors of extruded dilute Mg–Mn–Zn alloys

Creep and fracture behavior of as-cast Mg–11Y–5Gd–2Zn–0.5Zr (wt%)

High Temperature Creep Behavior of Mg-12Gd-2Y-2Sm-0.5Zr Magnesium Alloy