Abstract:This study highlights the importance of resin composition in ceramic stereolithographic 3D printing. Modulating the inclusion of a plasticizing agent and oligomer in the resin has significant effects on printed sample parameters such as cure depth and surface roughness. The choice of resin for ceramic stereolithographic 3D printing has a critical impact on printed ceramic preforms. In this study, we focused on the correlation between resin composition and parameters such as cure depth, surface morphology, lateral dimension, apparent layer height, and surface roughness. Special emphasis was placed on the addition of an oligomer and a plasticizing agent to a monomer‐based suspension. Four suspensions were studied: a 100% monomer (ethoxylated trimethylolpropane triacrylate) only suspension (M100), a suspension with 25% by weight plasticizing agent (polyethylene glycol) (PEG25), and two different suspensions with oligomer (urethane methacrylate) added at 25% (O25) and 50% (O50) by weight. Constant energy and printing parameters were used between suspensions. Adding a plasticizing agent (PEG25) was found to increase the cure depth and projected image of the samples, while additional oligomer with both amounts (O25 and O50) resulted in a decrease in the same parameters. The suspensions with oligomer were found to have increased surface roughness measured using the average deviation from the profile height mean line (Ra), with O25 at 13.47 μm and O50 at 11.47 μm. All suspensions had negative values of skewness (Rsk) in the range –0.4 to –1.2. PEG25 had the surface most distinct from a normally distributed surface with an Rsk of –1.12 and a kurtosis (Rku) value of 4.49. The use of the average length of a profile element (RSm) as a layer height estimation tool was explored and it was found that the RSm was within 10 μm of the printed layer height in all suspensions studied except for PEG25. This study highlights the importance of resin composition in ceramic stereolithographic 3D printing. Modulating the inclusion of a plasticizing agent and oligomer in the resin has significant effects on printed sample parameters such as cure depth and surface roughness.

The Influence of Ingredients of Silica Suspensions and Laser Exposure on UV Curing Behavior of Aqueous Ceramic Suspensions in Stereolithography

Effect of Optical Properties of Lithium Disilicate Glass Ceramics and Light-Curing Protocols on the Curing Performance of Resin Cement

Volume Shrinkage and Conversion Rate of Al2O3 Ceramic Stereolithography Suspension Polymerised by Ultraviolet Light

Relationship between the adhesion properties of UV-curable alumina suspensions and the functionalities and structures of UV-curable acrylate monomers for DLP-based ceramic stereolithography

Optimization of Curing Behavior of Si3N4 UV Resin for Photopolymerization 3D Printing

Research on the effects of surface modification of ceramic powder on cure performance during digital light processing (DLP)

Effect of Light Attenuation on Polymerization of Ceramic Suspensions for Stereolithography

Effect of reactive diluent concentration on rheological and curing behavior of zirconia ceramic slurry for DLP printing

Effect of siloxane quantity and ph of silane coupling agents and contact angle of resin bonding agent on bond durability of resin cements to machinable ceramic.

Formation mechanism of stereolithography of Si3N4 slurry using silane coupling agent as modifier and dispersant

Effects of exposure time and printing angle on the curing characteristics and flexural strength of ceramic samples fabricated via digital light processing

Effect of resin composition on cure depth, dimensional accuracy, and surface roughness in Al2O3 stereolithographic 3D printing

Curing behaviors and mechanical properties of SiC-whisker-reinforced alumina ceramics fabricated with digital light processing

The effect of light scattering in stereolithography ceramic manufacturing

Improving the accuracy of stereolithography 3D printed Al 2 O 3 microcomponents by adding photoabsorber: Fundamentals and experiments

Rheological behavior and curing deformation of paste containing 85 wt% Al2O3 ceramic during SLA-3D printing

Study of alumina ceramic parts fabricated via DLP stereolithography using powders with different sizes and morphologies

Cure behaviour and mechanical properties of Si3N4 ceramics with bimodal particle size distribution prepared using digital light processing

Design of a Shaping System for Stereolithography with High Solid Loading Ceramic Suspensions

Influence of boundary masks on dimensions and surface roughness using segmented exposure in ceramic 3D printing

Defect control in digital light processing of high-solid-loading ceramic core