Glass-Forming Ability, Crystallized Structure and Magnetic Properties of Fe67co9.5nd3dy0.5b20 Glassy Alloy with Large Supercooled Liquid Region

W Zhang,M Matsusita,CF Li,H Kimura,A Inoue

DOI: https://doi.org/10.2320/matertrans.42.2059

2001-01-01

MATERIALS TRANSACTIONS

Abstract:The glass-forming ability, thermal stability and magnetic properties have been investigated for a Fe67Co9.5Nd3Dy0.5B20 glassy alloy with a large supercooled liquid region of 48 K prepared by the melt-spinning technique. The glassy phase is formed in the wide sheet thickness range from 20 to 250 mum. The glass transition temperature (T-g), crystallization temperature (T-X), supercooled liquid region (DeltaT(X) = T-X - T-g) and heat of crystallization (DeltaH(c)) remain almost unchanged in the thickness range below 250 mum, and then the DeltaH(c) gradually decreases with further increasing sheet thickness. The crystallized nanocomposite structure consists of Fe3B, alpha -Fe, Nd2Fe14B and remaining glassy phase, and their average grain sizes are about 25 nm annealed at 903 K for 420 s. The remanence (B-r), coercivity (H-i(c)), and maximum energy product (B H)(max) are 1.26 T, 235 kA/m, and 104 kJ/m(3), respectively, for the sheet of 250 mum in thickness annealed at 903 K for 420 s. The hard magnetic properties remain almost unchanged in the thickness range below 250 mum, and decrease gradually in the sheets with thicknesses above 250 mum.