Field Electron Emission Improvement of ZnO Nanorod Arrays after Ar Plasma Treatment

Chun Li,Guojia Fang,Longyan Yuan,Nishuang Liu,Jun Li,Dejie Li,Xingzhong Zhao

DOI: https://doi.org/10.1016/j.apsusc.2007.04.040

IF: 6.7

2007-01-01

Applied Surface Science

Abstract:Vertically well-aligned single crystal ZnO nanorod arrays were synthesized and enhanced field electron emission was achieved after radio-frequency (rf) Ar plasma treatment. With Ar plasma treatment for 30min, flat tops of the as-grown ZnO nanorods have been etched into sharp tips without damaging ZnO nanorod geometrical morphologies and crystallinity. After the Ar ion bombardment, the emission current density increases from 2 to 20μAcm−2 at 9.0Vμm−1 with a decrease in turn-on voltage from 7.1 to 4.8Vμm−1 at a current density of 1μAcm−2, which demonstrates that the field emission of the as-grown ZnO nanorods has been efficiently enhanced. The scanning electron microscopy (SEM) results, in conjunction with the results of transmission electron microscopy (TEM), Raman spectroscopy and photoluminescence observation, are used to investigate the mechanisms of the field emission enhancement. It is believed that the enhancements can be mainly attributed to the sharpening of rod tops, and the decrease of electrostatic screening effect.