Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

Yield Criterion and Constitutive Model for Ductile Materials with Hydrogen and Deformation Induced Voids

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Fracture Strain Model for Hydrogen Embrittlement Based on Hydrogen Enhanced Localized Plasticity Mechanism

A Yield Criterion for Porous Crystalline Materials with Inner Pressure

Continuum Theory of Ductile Rupture by Void Nucleation and Growth: Part I—Yield Criteria and Flow Rules for Porous Ductile Media

A Constitutive Theory for the Damage of Materials with Dynamic Micro Void Evolution Processes.

A size-dependent ductile fracture model: Constitutive equations, Numerical implementation and Validation

Deformation and Damage Characteristics of Porous Materials under Different Triaxialities

A predictive model unifying hydrogen enhanced plasticity and decohesion

Research on the Constitutive Relation of Geomaterials Based on the Theory of Internal Variable

A self-consistent void-based rationale for hydrogen embrittlement

Theoretical, numerical and identification aspects of a new model class for ductile damage

A Phase-Field Regularized Cohesion Model for Hydrogen-Assisted Cracking

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel

LRI Model Lower-Bound Rigid-Plastic Constitutive Model for Isotropic-Hardening Materials with Micro Void Evolution Process.

Ductile rupture under cyclic loadings at high triaxiality: The influence of strain hardening and elasticity

Hydrogen Enhanced Intergranular Cracking -- A Phenomenological Multiscale Constitutive Model

Rigid–plastic Constitutive Theory for Normal Anisotropic and Planar Isotropic Sheet Metals with Voids

An uncoupled ductile fracture model considering void shape change and necking coalescence

Rigid plastic constitutive theory for porous materials including void evolution and mixed hardening effects

Ductile damage model for metal forming simulations including refined description of void nucleation