A Phase-Field Regularized Cohesion Model for Hydrogen-Assisted Cracking

Shiyi Zhang,Qiang Shen

DOI: https://doi.org/10.3390/coatings14020202

IF: 3.236

2024-02-05

Coatings

Abstract:Hydrogen-assisted cracking (HAC) usually causes premature mechanical failure of the material and results in structural damage in hydrogen environments. A phase-field regularized cohesion model (PF-CZM) was proposed to address hydrogen-assisted cracking. It incorporated the hydrogen-enhanced decohesion mechanism to decrease the critical energy release rate to address damage initiation and progression in a chemo-mechanical coupled environment. This model is based on coupled mechanical and hydrogen diffusion responses, driven by chemical potential gradients, and the introduction of hydrogen-related fracture energy degradation laws. The coupling problem is solved by an implicit time integral, in which hydrogen concentration, displacement and phase-field order parameters are the main variables. Three commonly used loading regimes (tension, shear, and three-point bending) were provided for comparing crack growth. Specifically, (i) hydrogen-dependent fracture energy degradation, (ii) mechanical–chemical coupling, and (iii) the diffusion coefficient D is influenced by both the phase field and the chemical field. By considering these factors, the PF-CZM model provided a variational framework by coupling mechanical loading with concentration diffusion for studying the complex interplay between a chemo-mechanical coupled environment and material damage, thereby enhancing our understanding of hydrogen-assisted cracking phenomena.

materials science, multidisciplinary,physics, applied, coatings & films

What problem does this paper attempt to address?

This paper attempts to solve the problem of Hydrogen - Assisted Cracking (HAC). Specifically, the paper proposes a Phase - Field Regularized Cohesion Model (PF - CZM) to describe the material damage and crack propagation behavior in a hydrogen environment. The following are the main research objectives and methods of the paper:

### Research Background
Hydrogen - Assisted Cracking is a common material degradation phenomenon, especially in metallic materials. The presence of hydrogen atoms significantly reduces the load - bearing capacity of the material, causing brittle fracture of the material under lower stress. This phenomenon has a significant impact on the mechanical properties and service life of the material.

### Research Objectives
1. **Propose a new model**: The paper proposes a Phase - Field Regularized Cohesion Model (PF - CZM), which combines the hydrogen - enhanced dissociation mechanism to reduce the critical energy release rate, thereby describing the damage initiation and propagation process of materials in a hydrogen environment.
2. **Couple chemical and mechanical effects**: The model is based on the coupling of mechanical response and hydrogen diffusion response. By driving the changes of hydrogen concentration, displacement and phase - field order parameter through the chemical potential gradient, the coupling problem is solved.
3. **Verify the validity of the model**: Verify the model's ability to predict crack propagation through three common loading modes (tensile, shear and three - point bending), and study the influence of chemical concentration erosion and mechanical loading on crack propagation behavior.

### Model Features
- **Hydrogen - dependent fracture energy degradation**: The model takes into account the influence of hydrogen concentration on the material fracture energy, and describes this process by introducing the hydrogen - dependent fracture energy degradation law.
- **Mechanochemical coupling**: The model takes into account the coupling effect of chemical concentration and mechanical damage, as well as the influence of these factors on the diffusion coefficient \( D \).
- **Phase - field method**: The phase - field method is used to describe the crack propagation process, avoiding the shortcomings of the traditional method that requires artificially setting the crack initiation and propagation criteria.

### Research Methods
1. **Phase - field model**: Define the phase - field variable \( \phi \), which is used to describe the transition area between the intact state and the completely fractured state of the material.
2. **Total potential energy**: Define the total potential energy function, including elastic strain energy and fracture surface energy, and take into account the influence of hydrogen concentration on the fracture surface energy.
3. **Governing equations**: Derive the governing equations, including equilibrium equations and boundary conditions, through the principle of virtual work and the law of energy conservation.
4. **Numerical simulation**: Verify the model's prediction ability under different loading modes through numerical simulation, and analyze the crack propagation, concentration diffusion and stress evolution processes.

### Conclusions
The Phase - Field Regularized Cohesion Model (PF - CZM) proposed in the paper can effectively describe the damage and crack propagation behavior of materials in a hydrogen environment, providing an important theoretical basis for understanding and preventing Hydrogen - Assisted Cracking. The model performs well under different loading modes, can accurately predict the crack propagation process and chemical concentration distribution, and is of great significance for optimizing structural design and material selection.