Abstract:Gelcasting is a new ceramic forming technology for making complex-shaped ceramic products with high performance. The processes used in gelcasting are similar to processes often used in conventional ceramic forming process. However, when new high performance materials are introduced with the aim to improve the strength, defects such as air bubbles or agglomerates that can be found in many traditional ceramic materials are no longer be allowed since this would reduce the performance and reliability of the final ceramic products. The aim of this thesis project was to find an appropriate recipe of the ceramic suspension meanwhile improving the process of gelcasting and obtaining ceramic products with excellent mechanical behavior. To achieve this specified target, alumina and zirconia powders were studied in the following experiments which included rheological measurement of viscosity and storage modulus measurement for ceramic suspensions and drying shrinkage measurement of cast materials. The binder was burned out and the density was measured for ceramic materials sintered at different temperatures. The mechanical strength of sintered materials with high density was evaluated and the microstructure of fracture surfaces of ceramic samples was studied. Through rheological measurement, a good balance between fluidity and solid content of ceramic suspension was found. For alumina suspensions a solid content of 55vol% was selected and for zirconia solid contents of 46, 48 and 50vol% were studied. A monomer was dissolved in the suspension and an initiator was added to facilitate the polymerization of the monomer when the temperature was increased to around 70oC. The failure analysis of the fractured bending bars showed that the defects that caused the failure were not air bubbles but agglomerates. As a result, in future research for ceramic gelcasting with the intention to improve the mechanical strength, the suggestion is to use an appropriate recipe for the ceramic suspension and focus on elimination of granules and agglomerates from the suspension

Study of Affecting Factors on Porosity in Gel-Casting Foam

Study on porosity of porous ceramics stirring-formed by gelcasting foams

Study on Porosity of Stiring-Formed by Gelcasting Foams

Factors affecting the microstructure of a fine ceramic foam

Relation Between Rheological and Curing Behavior of Inorganic Foam Slurries in the Gel-Casting Process

Porous Ceramic from Particle-Stabilised Foams Via Gelcasting

A Novel Method Based on Ultrastable Foam and Improved Gelcasting for Fabricating Porous Mullite Ceramics with Thermal Insulation–mechanical Property Trade-off

Fabrication of Porous Mullite Ceramics with High Porosity Using Foam-Gelcasting

PROPERTIES OF HIGHLY POROUS CORDIERITE CERAMIC OBTAINED BY DIRECT FOAMING AND GELCASTING METHOD

Factors Affecting the Pore Size in Porous Hydroxyapatite Produced by Stir-Froth-Polymerization Method

Gelcasting Preparation of Porous Silicon Nitride Ceramics by Adjusting the Content of Monomers

Processing, Microstructures and Mechanical Properties of Aqueous Gelcasted and Solid-State-Sintered Porous Sic Ceramics

Effects of Foaming Agent on Microstructure and Properties of Porous Mullite Ceramics

Investigation of Gel Casting Preparation of Micro-Porous Si_3N_4 Ceramics

Quantitative characterization and control mechanism of pore structure in geopolymer foams with addition of various surfactants

Preparation and Properties of Micro porous Si3N4 Ceramics by Gelcasting

Gel Casting of High Strength Ceramics

Effect of Foaming Pressure on the Properties of Porous Si3n4 Ceramic Fabricated by A Technique Combining Foaming and Pressureless Sintering

The controllable microstructure of porous Al2O3 ceramics prepared via a novel freeze casting route

Effects of Organic Additives on Microstructure and Mechanical Properties of Porous Si 3 N 4 Ceramics

Effect of holding time on the properties of porous ceramics with high-volume polished slag and its pore structure characteristics