Temperature Dependence of the Complete Material Coefficients Matrix of Soft and Hard Doped Piezoelectric Lead Zirconate Titanate Ceramics
Ribal Georges Sabat,Binu K. Mukherjee,Wei Ren,Guomao Yang
DOI: https://doi.org/10.1063/1.2560441
IF: 2.877
2007-01-01
Journal of Applied Physics
Abstract:We have used resonance methods to determine the variation of all the independent piezoelectric, elastic, and dielectric material coefficients, as well as the corresponding electromechanical coupling factors, of soft and hard doped piezoelectric lead zirconate titanate (PZT) ceramics with compositions near the morphotropic phase boundary, as a function of temperature ranging between −165 and 195°C. The material coefficients were obtained by analyzing the fundamental resonance of the impedance or admittance spectra as a function of frequency for several sample resonance geometries. The piezoelectric coefficients d33, −d31, and d15, as well as the dielectric permittivity coefficients ε11T and ε33T, generally increased with temperature for both soft and hard PZT samples. However, the elastic compliance coefficients s11E, −s12E, s33E, and s55E exhibited abnormal variations seen as broad peaks over parts of the tested temperature range. Additionally, thermal hystereses were observed in all the studied material coefficients over the temperature cycle. Finally, it was noted that, overall, the material coefficients of soft PZT varied significantly more than those of hard PZT under changing temperature conditions.