Effect of Raw Material and Process Conditions During the Dry Forming of CTMP Fibers for Molded Pulp Products
Eva Pasquier Kathrin Mörseburg Kristin Syverud Jost Ruwoldt RISE PFI AS,Trondheim,Norway
DOI: https://doi.org/10.1080/15440478.2024.2409890
2024-10-01
Journal of Natural Fibers
Abstract:This article provides a concise insight into the thermoforming of airlaid CTMP pulp. First, the airlaid process was studied, showing that fiber fractionation and the retention of fines occurred in the forming head. Then, the effect of temperature and pressure during thermoforming was investigated. Harsher conditions, i.e. higher temperature and pressure, yielded greater densification of the substrate and higher tensile strength. The maximum strength was found at the highest settings tested, that is, 100 MPa and 200°C. The screening of thermoforming conditions was also compared to previously published results on wetforming. Next, the effect of softwood CTMP pulp was delineated, which on average showed the best mechanical properties at elevated freeness and high degrees of bleaching. At last, a comparison between dry forming and wetforming was made for one selected pulp quality. Here, the dryformed substrates were stiffer at low elongation, yet the wetformed substrates yielded a greater extensibility and higher tensile strength. In conclusion, dryformed pulp mostly relies on temperature and pressure for bond formation during thermoforming, which produces materials that are distinctly different from wetformed molded pulp. 本文简要介绍了气流成网CTMP浆的热成型过程. 首先,对气流成网工艺进行了研究,结果表明纤维分馏和细粒滞留发生在成型头. 然后,研究了热成型过程中温度和压力的影响. 更苛刻的条件,即更高的温度和压力,使基材更致密,抗拉强度更高. 在测试的最高设置下,即100 MPa和200°C,发现了最大强度. 热成型条件的筛选也与之前发表的湿成型结果进行了比较. 接下来,描述了软木CTMP浆的效果,平均而言,它在高游离度和高漂白度下表现出最佳的力学性能。最后,对一种选定的纸浆质量进行了干法成型和湿法成型的比较. 在这里,干成型基材在低伸长率下更硬,但湿成型基材具有更大的延展性和更高的抗拉强度. 总之,干成型纸浆在热成型过程中主要依赖于温度和压力来形成粘合,这会产生与湿成型模塑纸浆明显不同的材料.
materials science, textiles