Abstract:The sole micropores strictly restrict the wide utilization of TS-1 zeolite in the catalytic fields, especially in the catalytic conversion of compounds with large molecular sizes. Here, we report a feasible and economical method to overcome this drawback. In this work, the hierarchical TS-1 zeolite was constructed via post-acid treatment, post-alkali etching, and a combination of post-acid treatment and alkali etching methods, after which, the corresponding NiMo-supported catalysts were prepared via the incipient wetness impregnation method. Then, the aforementioned materials were fully characterized using X-ray diffraction (XRD), N-2 adsorption-desorption, pyridine adsorbed Fourier transform infrared spectroscopy (Py - FTIR), H-2 temperature programmed reduction (H-2 - TPR), X-ray photoelectron spectroscopy (XPS), and high-resolution transition electron microscope (HR-TEM) to unravel the changes in the physicochemical properties caused by the post treatments. Finally, the hydrodesulfurization of dibenzothiophene (DBT) was used as a probe to assess the effects of the post-treatments on the catalytic performance of the hierarchical NiMo/TS-1 catalysts. The results showed that the MFI topology of TS-1 zeolite remained undamaged significantly and the serial hierarchical TS-1 zeolites exhibited higher specific surface areas and mesopore structures. Moreover, appropriate amounts of Bronsted acid sites were formed at the surface of the serial hierarchical TS-1 zeolites. The interaction between the active metals and the support materials was also modulated by the post-treatment of TS-1 zeolite, which resulted in better dispersion of Ni promoted MoS2 slabs with a higher proportion of NiMoS active phase, further leading to the enhanced catalytic activity and direct desulfurization pathway selectivity of the corresponding serial hierarchical NiMo/TS-1 catalysts. Among all the prepared catalysts, the catalytic activity was enhanced by approximately 1.2 times over catalyst NiMo/AT-TS-1 obtained by post-acid treatment compared to that over catalyst NiMo/TS-1 without treatment and on which the selectivity of the DDS pathway was 22% higher compared to that over catalyst NiMo/TS-1.

Nanosized titania and zirconia as catalysts for hydrolysis of carbon disulfide

Hierarchical TS-1 zeolite loaded with NiMo catalysts: Preparation and performance in hydrodesulfurization

Preparation and characterization of Cu/Ni/Fe hydrotalcite-derived compounds as catalysts for the hydrolysis of carbon disulfide

Catalytic Hydrolysis of Dichlorodifluoromethane over Nanosized Titania-Supported Titanyl Sulfate

In-situ Formed Stable Pt Nanoclusters on Ceria-Zirconia Solid Solutions Induced by Hydrothermal Aging for Efficient Low-Temperature CO Oxidation

Surface characterization of metal oxides-supported activated carbon fiber catalysts for simultaneous catalytic hydrolysis of carbonyl sulfide and carbon disulfide

Mesoporous Alumina Molecular Sieves: Characterization and Catalytic Activity in Hydrolysis of Carbon Disulfide

A Study on Catalytic Hydrolysis of Carbon Disulfide at Low Temperature

Nanosized Anatase TiO2 As Precursor for Preparation of Sulfated Titania Catalysts

Simple Solid Mixed Pt/TiO2-ZrO2 Catalyst for CO Oxidation with Excellent Sulfur and Water Resistance at Relatively Low Temperature

Low-temperature hydrolysis of carbonyl sulfide in blast furnace gas using Al2O3-based catalysts with high oxidation resistance

Preparation of MoS2 Nanocatalyst and Its Application in Hydrodesulfurization

Synthesis of Hydrophobic Nanosized Hierarchical Titanosilicate-1 Zeolites by an Alkali-Etching Protocol and Their Enhanced Performance in Catalytic Oxidative Desulphurization of Fuels

Design And Synthesis Of Metal Sulfide Catalysts Supported On Zeolite Nanofiber Bundles With Unprecedented Hydrodesulfurization Activities

Promoting Effects in Hydrogenation and Hydrodesulfurization Reactions on the Zirconia and Titania Supported Catalysts

Hierarchically Nanoporous TS-1 Zeolites for Catalytic Oxidation Desulfurization of Liquid Fuels

Low Temperature Catalytic Hydrolysis of Carbon Disulfide on Activated Carbon Fibers Modified by Non-thermal Plasma

Insight into H2S Production from CS2 Hydrolysis for Heavy Metals Treatment: In-situ FT-IR and DFT Studies over Crystalline Phase-Dependent ZrO2

States of Carbon Nanotube Supported Mo-Based HDS Catalysts

Activation of CO and Surface Carbon Species for Conversion of Syngas to Light Olefins on ZnCrO -Al2o3 Catalysts

Ultrasmall Cu Nanoparticles Supported on Crystalline, Mesoporous ZnO for Selective CO2 Hydrogenation