Abstract:By hydrogenating carbon dioxide to value-added products such as methanol, heterogenous catalysts can lower greenhouse gas emissions and generate alternative, liquid fuels. The most common commercial catalyst for CO2 reduction to methanol is Cu/ZnO/Al2O3, where ZnO improves conversion and selectivity toward methanol. The structure of this catalyst is thought to be Zn oxy(hydroxyl) overlayers at the nanometer scale on Cu. In the presence of CO2 and H2 under reaction conditions, the Cu substrate itself can be restructured and/or partially oxidized at its interface with ZnO, or the Zn might be reduced, possibly completely to a CuZn alloy, making the exact structure and stoichiometry of the active site a topic of active debate. In this study, we examine Zn3 clusters on Cu(100) and Cu(111), as a sub-nano model of the catalyst. We use a grand canonical genetic algorithm to sample the system structure and stoichiometry under catalytic conditions: T = 550 K, initial partial pressures of H2 = 4.5 atm and CO2 = 0.5 atm, and 1% conversion. We uncover a strong dependence of the catalyst stoichiometry on surface coverage. At the optimal 0.2 ML surface coverage, chains of Zn(OH) form on both Cu surfaces. On Cu(100), the catalyst has many thermally accessible metastable minima, whereas on Cu(111), it does not. No oxidation or reconstruction of the Cu is found. However, at lower coverage of Zn, Zn3 clusters take on a metallic form on Cu(100), and slightly oxidized Zn3O on Cu(111), while the surface uptakes H to form a variety of low hydrides of Cu. We thus hypothesize that the reason the 0.2 ML Zn coverage is optimal, as found experimentally, is the stronger yet incomplete oxidation afforded by Zn at this coverage.

Ultrasmall Cu Nanoparticles Supported on Crystalline, Mesoporous ZnO for Selective CO2 Hydrogenation

Bifunctional Catalysts Composed of Low Silicon‐content SAPO‐34 Nanosheets and in 2 O 3 /zro 2 with Improved Performance for CO 2 Hydrogenation

Hollow structured Cu@ZrO2 derived from Zr-MOF for selective hydrogenation of CO2 to methanol

Bimetallic CuPd nanoparticles supported on ZnO or graphene for CO2 and CO conversion to methane and methanol

Confinement of Ultrasmall Cu/ZnOx Nanoparticles in Metal-Organic Frameworks for Selective Methanol Synthesis from Catalytic Hydrogenation of CO2

The Activity of Ultrafine Cu Clusters Encapsulated in Nano-Zeolite for Selective Hydrogenation of CO2 to Methanol

Optimization and understanding of ZnO nanoarray supported Cu-ZnO-Al2O3 catalyst for enhanced CO2 -methanol conversion at low temperature and pressure

A highly efficient Cu/ZnOx/ZrO2 catalyst for selective CO2 hydrogenation to methanol

Core–shell structured Cu@m-SiO2 and Cu/ZnO@m-SiO2 catalysts for methanol synthesis from CO2 hydrogenation

Effect of the Cu/ZnO/SBA‐15/kaolinite Preparation Method on the Catalyst Structural Properties and Catalytic Performance at CO2 Hydrogenation at Low Pressure

Cu-supported ZnO in Conditions of CO2 Reduction to Methanol: Why 0.2 ML Coverage?

Precise Confinement and Position Distribution of Atomic Cu and Zn in ZSM-5 for CO2 Hydrogenation to Methanol

Conversion of Carbon Dioxide into Methanol Using Cu–Zn Nanostructured Materials as Catalysts

Hybrid Catalyst Coupling Zn Single Atoms and CuNx Clusters for Synergetic Catalytic Reduction of CO2

High-Performance Cu/ZnO/Al 2 O 3 Catalysts for CO 2 Hydrogenation to Methanol

Cu-Supported ZnO under Conditions of CO 2 Reduction to Methanol: Why 0.2 ML Coverage?

Low-Temperature Hydrogenation of CO2 to Methanol in Water on ZnO-Supported CuAu Nanoalloys

Ultrasmall Ni Nanoparticles Embedded in Zr-based MOFs Provide High Selectivity for CO2 Hydrogenation to Methane at Low Temperatures

Copper nanoparticles encapsulated in zeolitic imidazolate framework-8 as a stable and selective CO2 hydrogenation catalyst

Investigation of Cu-ZnO/SiO2 Catalysts for CO2 Hydrogenation: Effect of SiO2 Support with Different Porous Structure

Cu/ZnO/Al2O3 Catalyst Modulated by Zirconia with Enhanced Performance in CO2 Hydrogenation to Methanol