Abstract:Rare earth conversion coating was proposed as one of the most prospective alternatives to toxic chromate conversion coatings on some metals and alloys. In this work. the lanthanum salt conversion coating was obtained by immersing a galvanized steel in a lanthanum salt passivation solution modified with citric acid. Scanning electron microscopy (SEM), X-ray energy dispersive spectrometer (EDS), X-ray photoelectron spectroscopy (XPS) and infrared spectroscopy (IR) were used to investigate its structure and composition. Neutral salt spray (NSS) tests were used to evaluate the anti corrosive performance of the coating and the optimum range of treatment time. The results show that the lanthanum salt conversion coating modified with citric acid mainly consists of LaCit, La(OH)(3)/La2O3 and a trace of Zn(OH)(2)/ZnO. When treatment time is more than 10 min, the modified coating on the samples consists of two layers: the inner layer is compact mid the outer lanthanum-riched layer is thin and poriferous. Cracks occur in the coating when treatment time within s and are evolved during further treatment. The thickness of the coating obtained on galvanized steel that the immersion time is 1 min is approximately 250 urn, and increasing with treatment time within 60 min. The growing rate of the coating is faster than that of conversion coatings without modified with citric acid. The growth process of the coating can be divided into three stages: at the initial time complexes ions of lanthanum citrate were adsorbed on the whole surface of galvanized steel. then lanthanum citrate and lanthanum hydroxide are co-deposited on surface, and in the final stage there is lanthanum hydroxide mainly deposited on surface of the coating. The corrosion resistance of the coating is close to that of a chromate conversion coating. The optimum treatment time is 10 to 30 min.

Synergistic effect of rare earth salt and organic acid in the anodization of aluminum in phosphoric acid

Corrosion resistance of anodically oxidized LY12 aluminum alloy after modification with cerium nitrate and silane

Influence of Acid Pickling on Electrodeposition of Aluminum on Magnesium Alloy in Room Temperature Molten Salts

Electrodeposition of aluminum on rare earth alloy surface in room temperature molten salts

Influence of oxalic additive on etidronic acid anodizing of aluminum alloy

Effects of tartaric acid on the structure and corrosion resistance for anodizing films of aerospace aluminium alloys

Improved corrosion resistance of PEO-coated 7085Al alloy via a novel organic and inorganic sealing-treatment combination

Rare Earth Application in Sealing Anodized Al-Based Metal Matrix Composites

Analysis and self-lubricating treatment of porous anodic alumina film formed in a compound solution

Synergistic effect of an organic hydrophobic film deposited on MAO containing NaH 2 PO 4 for enhanced corrosion resistance of 6063 aluminum alloy

Analysis on porous aluminum anodic oxide film formed in Re–OA–H3PO4 solution

Hydrothermal and cerium salt sealing of a 6061 aluminum alloy

Insight for Microstructure Research of Materials

Influence of synergistic effect of phosphate on corrosion resistance of self-assembled superhydrophobic composite film on 6061 aluminum alloy surfaces

Anodic Layer Growth on 1050 and 2024 Aluminium Alloys in Presence of Etidronic Acid : Changes in Morphology and Structure

Electrodeposition of cerium (III)-modified bis-[triethoxysilypropyl]tetra-sulphide films on AA2024-T3 (aluminum alloy) for corrosion protection

Boric/Sulfuric Acid Anodizing of Aluminum Alloys 2024 and 7075: Film Growth and Corrosion Resistance

Effect of Oxalic Acid Additives on Aluminum Anodizing in Formic Acid Containing Ammonium Heptamolybdate

Study on the rare earth sealing procedure of the porous film of anodized Al6061/SiCp

Electrochemical Study of Corrosion Behavior of Rare Earth Based Chemical Conversion Coating on Aerospace Aluminum Alloy

The Mechanism of Solution Acidification During Chemical Conversion Process on Aluminium Alloys