Preparation of porous β-SiAlON ceramics using corn starch as pore-forming agent
Xin Liu,Chen Yu,Dianli Qu,Xudong Luo
DOI: https://doi.org/10.1007/s41779-022-00708-3
2022-02-12
Journal of the Australian Ceramic Society
Abstract:In this study, porous β-SiAlON ceramics were prepared by starch consolidation using corn starch as a pore-forming agent. The effect of corn starch content (10 wt.%, 20 wt.%, and 30 wt.%) on the microstructure, apparent porosity, compressive strength, and dielectric properties of porous β-SiAlON ceramics was investigated. It was observed that both β-SiAlON and corundum phases were present in the prepared porous β-SiAlON ceramics. Meanwhile, the SEM results revealed that the hierarchical pore structures were formed as the corn content was enhanced. Increasing the corn starch content from 10 to 30 wt.% enhanced the apparent porosity from 53 to 64%, whereas the compressive strength decreased from 6.5 to 3.8 MPa. The porous β-SiAlON ceramics consisting of 60 wt.% solid content and 30 wt.% corn starch possessed porosity of 64%, reasonable compressive strength of 3.8 MPa, low dielectric constant of 3.0, and low dielectric loss tangent of 0.0046. Overall, the obtained results confirm that the starch consolidation method is a simple and convenient approach for preparing porous β-SiAlON ceramics with potential application in the field of radome.
materials science, ceramics