Abstract:In this research, we creatively integrate the traditional methods of liquid precursor infiltration plus in situ precipitation with stereolithography-based 3D printing for the fabrication of Al2O3-ZrO2 ceramics to ensure the homogeneous distribution of ZrO2 particle in the alumina matrix. Our characterization results shows that this combination leads to the materials with significantly better performance. The Al2O3 specimen is soaked in a Zr4+ ion solution to induce infiltration, in-situ precipitation and then sintered. X-ray diffraction analysis of the thus-treated sample indicated that Al2O3 was the primary phase and t-ZrO2 was the secondary phase. Microstructural and EDS analysis showed that the ZrO2 particles were homogeneously distributed in the Al2O3 matrix, leading to inhibited grain growth. The samples soaked in solutions for different Zr4+ concentrations and sintered both at 1450 degrees C and 1550 degrees C showed improved mechanical properties as compared to those of pure alumina. Futhermore, the sample infiltrated using the solution with a concentration of 1.5 mol/L and sintered at 1450 degrees C showed similar fracture toughness (4.97 MPa m(1/2)) with the sample sintered at 1550 degrees C (5.06 MPa m(1/2)) but much better hardness (20.95 Gpa) than the sample sintered at 1550 degrees C (19.71 GPa). Therefore, this method could not only enhance the mechanical properties via introducing the second phase, but also lowers the sintering temperature by at least 100 degrees C, which would be beneficial for energy conservation and leads to significant advances in the 3D printing of ceramic components. (C) 2018 Elsevier B.V. All rights reserved.

Fabrication of Porous Fibrous Alumina Ceramics by Direct Coagulation Casting Combined with 3D Printing

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Fabrication of Porous Alumina Ceramics with Directional Pore Channels Structure by Freeze-Gel Casting Processing

Fabrication of porous aluminum ceramics beyond device resolution via stereolithography 3D printing

Fabrication and properties of porous alumina ceramics with three different pore sizes

Fabrication of alumina ceramics with high flexural strength using stereolithography

Preparation of Porous Ceramic Materials by Alumina Fiber Framework

Fabrication of Al2O3 ceramic cores with high porosity and high strength by vat photopolymerization 3D printing and sacrificial templating

Air permeable alumina-based porous ceramics with high performance prepared by novel gel casting route

Fabrication and mechanical properties of triply period minimal surface porous alumina ceramics based on Digital Light Processing 3D printing technology

Effect of Holding Time During Sintering on Microstructure and Properties of 3D Printed Alumina Ceramics

Enhanced 3D Printed Alumina Ceramic Cores Via Impregnation

High-strength porous alumina ceramics prepared from stable wet foams

Hierarchically porous Al2TiO5 ceramics via freeze-gel casting

Preparation of porous alumina ceramic with ultra-high porosity and long straight pores by freeze casting

Fabrication of High-Performance Al2O3-ZrO2 Composite by a Novel Approach That Integrates Stereolithography-Based 3D Printing and Liquid Precursor Infiltration

FABRICATION OF POROSITY GRADIENT ALUMINA CERAMICS BY THE CENTRIFUGAL CASTING METHOD

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

Preparation of high performance dense Al 2 O 3 ceramics by digital light processing 3D printing technology