Abstract:As a classic ferroelectric material, orthorhombic perovskite KNbO3 demonstrates a large electro-optical coefficient, high refractive index, and excellent nonlinear optical property. These make single-crystal KNbO3 films being long-pursued for lead-free sensor or optoelectronic device applications. However, it remains a challenge to obtain high-quality single-crystal KNbO3 films because of the volatility of potassium at a high growth temperature. In this work, single-crystal KNbO3 films with a tunable thickness have been successfully fabricated by a low-temperature (∼220 °C) hydrothermal epitaxy on cubic single-crystal Nb:SrTiO3 substrates. Interestingly, the KNbO3 film was investigated to adopt a single-domain structure with a polarization direction pointing to the substrate. In-depth characterization reveals an intriguing disordered region of approximately 0.6–1.2 nm because of partial Nb substitution of Ti near the interface, giving rise to the coexistence of Ti3+ and Ti4+ ions. Such region is proposed to release a large interface strain energy from a large lattice misfit (∼2.3%) between {011}KNbO3 and {100}Nb:SrTiO3 and reduce interfacial electrostatic energy via screening of the positive polar surface of KNbO3. This allows to drive a hydrothermal epitaxy of single-crystal and single-domain KNbO3 without forming a typical dislocation. The films demonstrate a great photovoltaic short-circuit current of 15.65 μA/cm2 under the 375 nm laser irradiation of 500 mW/cm2 light intensity, and the corresponding photoresponsivity is the highest among the emerged KNbO3-based materials. Such improvement in the photoresponsivity has been attributed to a successful low-temperature solution epitaxy of single-crystal and single-domain KNbO3 films, where K deficiency can be significantly suppressed. These findings suggest that a solution epitaxy strategy is effective in producing high-quality ferroelectric films for lead-free optoelectronic or self-powered photodetector device applications.

Large-scale Synthesis of Single-Crystalline KNb3O8 Nanobelts Via a Simple Molten Salt Method

A Simple Molten Salt Method to Synthesize Single-Crystalline Potassium Titanate Nanobelts

Potassium Molten Salt-Mediated In Situ Structural Reconstruction of a Carbon Nitride Photocatalyst.

Electrical and Photocatalytic Properties of Na2Ti6O13 Nanobelts Prepared by Molten Salt Synthesis

Molten Salt Assisted Synthesis of Boron Carbon Nitride Nanosheets for Enhanced Photocatalytic Activity of Silver Phosphate

A facile molten salt route to K2Nb8O21 nanoribbons

Hydrothermal Synthesis of Bamboo-Shaped Nanosheet KNb3O8 with Enhanced Photocatalytic Activity

Novel Synthesis of Polymorphous Nanocrystalline KNbO3 by a Low Temperature Solution Method

Size-tunable synthesis of ferroelectric KNbO3 nanowires

Short Communication A Facile Molten Salt Route to K2Nb8O21 Nanoribbons

Key to Enhance Thermoelectric Performance by Controlling Crystal Size of Strontium Titanate

Low-Temperature Synthesis of Nanocrystalline KNbO3

Polarization-gradient KNbO3 Film with a Large Photovoltaic Current

Low temperature synthesis and characterization of substitutional Na-modified K2Ti6O13 nanobelts with improved photocatalytic activity under UV irradiation

Synthesis of nitrogen-doped KNbO3 nanocubes with high photocatalytic activity for water splitting and degradation of organic pollutants under visible light

Synthesis and Characterization of Nanocrystalline Niobates

Synthesis of Single-Crystalline Niobate Nanorods Via Ion-Exchange Based on Molten-Salt Reaction

Solution epitaxy of single-crystal and single-domain KNbO3 film with a great photovoltaic current

Synthesis of Potassium Sodium Niobate Nanostructures by Hydrothermal Combining with the Sol-Gel Method

Single-crystalline Orthorhombic Molybdenum Oxide Nanobelts: Synthesis and Photocatalytic Properties

Novel (na, K)Tao3 Single Crystal Nanocubes: Molten Salt Synthesis, Invariable Energy Level Doping and Excellent Photocatalytic Performance