Abstract:The aluminum oxyhydroxide boehmite is an important crystalline phase in nature and industry. We report development of a flexible additive-free hydrothermal synthesis method to prepare high quality boehmite nanoplates with sizes ranging from under 20 nm 5 mu m to via using hydrated alumina gels and aluminum hydroxide amorphous powders as precursors. The size and morphology of the boehmite nanoplates was systematically varied between hexagonal and rhombic by adjusting precursor concentrations, pH, and the synthesis temperature, due to face-specific effects. The transformation mechanism is consistent with dissolution and reprecipitation, and involves transitory initial appearance of metastable gibbsite that is later consumed upon nucleation of boehmite. Detailed X-ray pair distribution characterization of the solids over time showed similarities in short-range order that suggest linkages in local chemistry and bonding topology between the precursors and product boehmite, yet also that precursor-specific differences in long-range order appear to manifest subtle changes in resulting boehmite characteristics, suggesting that the rate and extent of water release or differences in the resulting solubilized aluminate speciation lead to slightly different polymerization and condensation pathways. The findings suggest that, during dissolution of the precursor, precursor-specific dehydration or solution speciation could be important aspects of the transformation impacting the molecular-level details of boehmite nucleation and growth.

Large-area synthesis of single-crystal boehmite nanobelts with high luminescent properties

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Hydrothermal synthesis of microscale boehmite and gamma nanoleaves alumina

Controlled synthesis and luminescence of semiconductor nanorods.

Facile and large-scale synthesis of single-crystalline manganese oxyhydroxide/oxide nanostructures

Hydrothermal synthesis of ZnO nanowires and nanobelts on a large scale

Hierarchical nanoarchitectonics of boehmite: The preparation of three-dimensional flower-like via hydrothermal method without surfactants

Short belt-like Ca2B2O5·H2O nanostructures: Hydrothermal formation, FT-IR, thermal decomposition, and optical properties

A General Approach to Functional Metal Oxide Nanobelts: Thermal Decomposition of Precursors and Interface Diffusion Growth Mechanism

Hydrothermal Preparation Of Boehmite Nanorods By Selective Adsorption Of Sulfate

Morphological Controlled Growth of Nanosized Boehmite with Enhanced Aspect Ratios in an Organic Additive-Free Cationic–Anionic Double Hydrolysis Method

A self-seeded, surfactant-directed hydrothermal growth of single crystalline lithium manganese oxide nanobelts from the commercial bulky particles

Controlled Growth of Large-Area, Uniform, Vertically Aligned Arrays of α-Fe<sub>2</sub>O<sub>3</sub>Nanobelts and Nanowires

Hydrothermal Synthesis of Single Crystal Mesoporous LiAlO2 Nanobelts

A new route to synthesis of γ-alumina nanorods

Mechanical force-driven growth of elongated BaTiO3 lead-free ferroelectric nanowires

Facile Synthesis of Hierarchical Nanosized Single‐Crystal Aluminophosphate Molecular Sieves from Highly Homogeneous and Concentrated Precursors

Hydrothermal synthesis of single-crystal szaibelyite MgBO2(OH) nanobelt as a new host material for red-emitting rare-earth ions

Polymer-directed large-scale synthesis of single-crystal vanadium oxide nanobelts

Controlled growth of large-area, uniform, vertically aligned arrays of alpha-Fe2O3 nanobelts and nanowires.