Preparation and Characterization of Poly(vinyl Pyrrolidone)/fe3o4 Composite Nanofibers

Li Xiang,Zhao Yi-Yang,Lu Xiao-Feng,Wang Hai-Ying,Wang Ce
DOI: https://doi.org/10.3321/j.issn:0251-0790.2006.10.052
2006-01-01
Abstract:Poly(vinyl pyrrolidone) (PVP)/Fe3O4 composite nanofibers were successfully prepared by using electrospinning technique. The composite nanofibers were characterized by means of TEM(transmission electron microscopy), XRD(X-ray diffraction) and TGA(thermogravimetric analysis). Transmission electron microscope images of the PVP/Fe3O4 nanofibers show that the Fe3O4 nanoparticles with a diameter about 10.5 nm were dispersed in PVP fiber matrices. The XRD results show that the particles in PVP fibers were indeed Fe3O4 nanoparticles. And the TGA of PVP/Fe3O4 nanofibers show that the content of Fe3O4 nanoparticles in the composite was about 36.8% (mass fraction). The PVP/Fe3O4 nanofibers were found to be superparamagnetic. The hysteresis loop at room temperature showed a high saturated magnetization (M-s = 15.1 emu/g) and a low coercive force(mu(c) =0).
What problem does this paper attempt to address?