Fabrication and Characterization of LaCoO3 Nanofibers Via an Electrospinning Technique
Jinxian Wang,Xiangting Dong,Zhen Qu,Guixia Liu,Wensheng Yu
DOI: https://doi.org/10.5539/ijc.v2n1p161
2010-01-01
International Journal of Chemistry
Abstract:Polyvinyl alcohol(PVA)/[La(NO 3 ) 3 +Co(CH 3 COO) 2 ] composite nanofibers were prepared by combination of sol-gel method and electrospinning technique, and crystalline LaCoO 3 nanofibers were fabricated by calcination of the PVA/[La(NO 3 ) 3 +Co(CH 3 COO) 2 ] composite nanofibers at 600ºC for 10h.The samples were characterized by using thermogravimetric-differential thermal analysis(TG-DTA), X-ray diffraction spectrometry(XRD), scanning electron microscopy(SEM) and Fourier transform infrared spectrometry(FTIR).The results show that PVA/[La(NO 3 ) 3 +Co(CH 3 COO) 2 ] composite nanofibers are amorphous in structure, and pure phase LaCoO 3 nanofibers are trigonal in structure with space group m R3 .The surface of as-prepared composite nanofibers is smooth, and the diameter is about 200nm.The diameter of LaCoO 3 nanofibers is smaller than that of the relevant composite fibers.The surface of the LaCoO 3 nanofibers becomes coarse with the increase of calcination temperatures.The diameter of LaCoO 3 nanofibers is ca.80nm, and the length is greater than 100μm.The mass of the sample remains constant when the temperature is above 500ºC, and the total mass loss percentage is 83%.Possible formation mechanism of LaCoO 3 nanofibers is preliminarily proposed.