Corrosion Behavior of Extruded Near Eutectic Al–Si–Mg and 6063 Alloys

Yuna Wu,Hengcheng Liao

DOI: https://doi.org/10.1016/j.jmst.2013.02.001

2013-01-01

Abstract:In this work,a comparison study on corrosion behavior of extruded near eutectic Al—12.3%Si—0.26%Mg and 6063 alloys has been carried out by mass loss test in 4%H 2 SO 4 aqueous solution in the open air and potentiodynamic polarization test in 3.5 wt.%NaCI aqueous solution.Results indicate that the corrosion resistance of the near eutectic Al—Si—Mg alloy is less than that of 6063 alloy.Macro/microscopy and scanning electron microscopy results clearly show the difference of the corrosion progress of these two alloys in 4%H 2 SO 4 aqueous solution.The corrosion type of 6063 alloy is pitting corrosion.The Mg 2 Si and AlFeSi particles and surface defects act as nucleation sites for pitting,and the amount and distribution of them have a significant effect on the pitting behavior.For the near eutectic alloy,there are two types of corrosion cells. One is between the extruded primaryα-AI and the eutectic,the other is between the eutectic Al and eutectic Si particles.Combination of these two types of corrosion cells leads to a lower corrosion resistance,a higher mass loss of the near eutectic alloy compared with 6063 alloy,and the formation of the paralleling corroded grooves.