Damage-tolerant Laminated Composites in Thermal Shock

Z. Chen,J. J. Mecholsky

DOI: https://doi.org/10.1007/bf01352199

IF: 4.5

1993-01-01

Journal of Materials Science

Abstract:Alumina is very susceptible to thermal shock which often leads to catastrophic failure. The addition of tape-cast nickel layers to laminated alumina can increase its tolerance to damage induced during thermal shock. The fracture behaviour after thermal shock of laminated composites showed non-catastrophic failure during loading at room temperature. The retained strength of the laminates was determined for a wide range of quenching-temperature differences (δT= 150–1200‡C). The retained strength and critical quenching-temperature difference, δTc, of the laminated composites were a significant improvement over the values for the respective monolithic alumina. This improvement in behaviour can be related to the compressive residual stress in the alumina layers and ductile-layer crack blunting.