Abstract:Microstructure, texture evolution and mechanical properties of extruded Mg-4.58Zn-2.6Gd-0.18Zr alloy were investigated at extrusion temperatures of 260 °C, 280 °C and 300 °C, extrusion ratios of 10, 15 and 30, and ram speeds of 3 mm s−1 and 6 mm s−1, respectively. The results indicated that the as-cast experimental alloy was composed of α-Mg matrix, coarse α-Mg + W(Mg3Zn3Gd2) eutectic and icosahedral quasicrystalline I(Mg3Zn6Gd) phase. A small amount of undissolved W phases were detected after the homogenization treatment at 505 °C up to 16 h, while most I phase dissolved into the α-Mg matrix. The initial crystallites before extrusion were randomly oriented, and showed a typical random texture. After extrusions, all samples exhibited a bimodal microstructure consisting of fine Dynamic recrystallization (DRX) grains and coarse elongated un-DRX grains, and the formation of ultra-fine DRX grains only occurred in the sample with an extrusion ratio of 10 at 260 °C, 3 mm s−1, which was caused by the solute segregation in homogenized billets and non-uniformly distributed W phase during the extrusion process. A fiber texture with {0002} planes and <1̄21̄0> directions paralleled to the extrusion direction was observed to be dominant in all the extruded samples. Furthermore, the increase of extrusion ratio was found to be beneficial for the DRX process and refinement of grain size, and the maximum texture intensity was accordingly weakened, which resulted in a decrease of tensile yield strength but an increase of elongation. With increasing the extrusion temperature or ram speed, both the grain size and DRX fraction gradually increased. Consequently, the texture was randomized and the maximum texture intensity decreased, which led to a reduction of the elongation and tensile yield strength. The tensile failure behaviors under different extrusion conditions were found to be related with the contraction twin lamellas formed in the un-DRX grains and the string-like W phases.

The Influence of Developed Texture on the Mechanical Anisotropy and Deformation Modes of an As-Extruded Mg-Zn-Zr Alloy

The influence of initial texture, microstructure and deformation behavior on the low mechanical anisotropy of extruded Mg alloy tube

Effects of Bimodal Basal Texture on Bending Stress and Microstructure Evolution of Mg-2.6Nd-0.55Zn-0.5Zr Alloys

Texture Evolution and Deformation Activity of an Extruded Magnesium Alloy: Effect of Yttrium and Deformation Temperature

Deformation Behavior and Texture Evolution in an Extruded Mg-Li Sheet with Non-Basal Texture During Tensile Deformation

Effects of Deformation Mechanisms on Texture Evolution and Mechanical Response of the Mg-1Al-0.5Mn-0.3Gd Alloy Under Plane Tension

The microstructure evolution and mechanical anisotropy of extruded Mg-2Zn-0.4Ce-0.4Mn alloy tube during tension in different directions

Effect of texture types on microstructure evolution and mechanical properties of AZ31 magnesium alloy undergoing uniaxial tension deformation at room temperature

Effects of extrusion die cavity on the texture components and the associated mechanical properties for ZK60 magnesium alloy

Effect of Microstructure and Texture on the Mechanical Properties of the As-Extruded Mg–Zn–Y–Zr Alloys

Texture Evolution and Their Effects on the Mechanical Properties of Duplex Mg–Li Alloy

Microstructure, Texture Evolution and Tensile Properties of Extruded Mg-4.58Zn-2.6Gd-0.16Zr Alloy

Asymmetric Tension-Compression Mechanical Behaviors of Extruded Mg-4.58Zn-2.6Gd-0.18Zr Alloy with Double-Peak Fiber Texture

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Ex-situ EBSD Analysis of Yield Asymmetry, Texture and Twinning Development in Mg–5Li–3Al–2Zn Alloy During Tensile and Compressive Deformation

Achieving High Ductility and Low In-Plane Anisotropy in Magnesium Alloy Through a Novel Texture Design Strategy

Unique Deformation Mechanisms of Extruded Mg-Y-Sm-Zn-Zr Alloy

Effects of Texture on Tensile Property of Extruded Az31 Magnesium Alloy Investigated by Acoustic Emission

Formation of an abnormal texture in Mg-Gd-Y-Zn-Mn alloy and its effect on mechanical properties by altering extrusion parameters

Anisotropy of thermal conductivity and mechanical properties in Mg-5Zn-1Mn alloy

Tensile Properties, Texture Evolutions and Deformation Anisotropy of As-Extruded Mg-6Zn-1Zr Magnesium Alloy at Room and Elevated Temperatures