Abstract:In this paper, Zr, Cr and V were selected as the partial substitution elements for Ti to form Mg35Ti5M5Ni55 quaternary alloys prepared by means of mechanical alloying on the basis of the ternary Mg35Ti10Ni55 electrode alloy previously studied by the authors. It is found that all the three quaternary alloys possess an amorphous main phase and exhibit improved cycling stability than the original ternary Mg35Ti10Ni55. The Zr-substituted alloy has also a higher discharge capacity. X-ray photoelectron spectroscopy (XPS) surface analysis reveals that on the surface of each alloy a multi-component oxide composite film is formed, which is more compact and corrosion resistant than the Mg(OH)2 film and the (TiO2)x(NiO)y(Mg(OH)2)z composite films reported previously. Auger electron spectroscopy (AES) analysis shows that the substituting elements tend to reduce the thickness of the passivation films. The thickness of composite oxide film on the alloys is in the following order: Mg35Ti10Ni55>Mg35Ti5V5Ni55>Mg35Ti5Zr5Ni55>Mg35Ti5Cr5Ni55. The result agrees well with that of the polarization resistances (RP) values obtained from the electrochemical impedance spectroscopy (EIS) Nyquist diagrams. It demonstrates that the thicker the passivation film is, the higher the RP is and the more difficultly the charge transfer reaction proceeds. Anodic polarization curves indicate that the addition of Cr and Zr decreases effectively the corrosion current. However, the corrosion of the electrode alloys in the electrolyte is still high and proceeds constantly as the corrosion current remains almost constant during further cycles.

Activation behavior of Zr0.7Ti0.3Cr0.3Mn0.3V0.4Ni alloy electrode modified by the hot-charging treatment

Improved electrochemical performance of AB2-type metal hydride electrodes activated by the hot-charging process

Surface Modification for La1-Xcex(Nicomnal)(5) Hydride Electrode by Hot Charging in Potassium Borohydride Solution

Effect of Quenching Treatment on the Phase Structure and Electrochemical Properties of V2.1TiNi0.4Zr0.06Mn0.05 Alloy

The Effects of Partial Substitution of Mn by Cr on the Electrochemical Cycle Life of Ti-Zr-V-Mn-Ni Alloy Electrodes of a Ni/MH Battery

Cyclic voltammetry and electrochemical impedance of MmNi3.6Co0.7Mn0.4Al0.3 alloy electrode before and after treatment with a hot alkaline solution containing reducing agent

Effects of heat-treatment temperature on microstructure and electrochemical properties of AB5 type MlNi 3.60Co 0.85Mn 0.40Al 0.15 hydride electrode alloy

The hydrogen evolution reaction during charging for Ti–Zr–V–Ni–Cr alloy electrode

Surface treatment for hydrogen storage alloy of nickel/metal hydride battery

New Surface Modification for La_(1-x) Ce_x(NiCoMnAl)_5 Hydrogen Storage Alloys: KBH_4 Alkaline Aqueous Solution-Hot Charging Treatment

Effect of magnetization treatment on the electrochemical properties of La0.9Sm0.1Ni2.0Co3.0 electrode alloy

Surface Modification and Preparation Technique for La_(1- X) Ce_x (nicomnal)_5 Hydrogen Storage Alloy Electrode

Electrochemical Investigations of Activation and Degradation of Hydrogen Storage Alloy Electrodes in Sealed Ni/MH Battery

The effect of partial substitution of Ti with Zr, Cr or V in the Mg35Ti10Ni55 electrode alloy on its electrochemical performance

Electrochemical Behaviors Of A V3tini0.5hf0.24 Alloy Electrode During Charge-Discharge Cycling

The Effects of Partial Substitution of Mn by Cr on the Phase Structure, Microstructure and Electrochemical Properties of Ti-Zr-V-Mn-Ni Hydrogen Storage Alloys

The effects of mechanical grinding on the hydrogen storage properties of MlNi4.7Al0.3 alloy

Surface treatments of hydrogen storage alloy improve charge-discharge performances of Ni/MH battery

Improvement of the electrochemical properties of Zr-based AB2 alloys by an advanced fluorination technique

New surface modification of Zr Ti hydrogen storage alloys

A wet ball milling treatment of Zr-based AB2 alloys as negative electrode materials