Experimental Study on Compressive Behavior of Compressive Stress-Loaded Concrete at Different Strain Rates under Simulated Acid Rain Environment
Yingzi Zhang,Shitong Zhuang,Mingbo Qu,Qinghe Fang,Qingli Zhao,Guofang Chen
DOI: https://doi.org/10.1016/j.jobe.2024.110584
IF: 7.144
2024-01-01
Journal of Building Engineering
Abstract:Concrete is typically under stress when exposed to acid rain corrosion. This study aimed to assess the physical and compressive behavior of compressive stress-loaded concrete (CSLC) under a simulated acid rain environment. The compressive stress states (0 %, 15 %, 20 %, 25 %, and 30 % of its compressive strength) and a simulated acid rain environment (pH = 2) were replicated in the laboratory. A compression tester was used to control loading at different strain rates (0.5 x 10-3/s, 10-3/s, 10- 2/s, and 10- 1/s). The results elucidate a three-stage pattern in the mass degradation of CSLC, accompanied by shallower corrosion depth compared to unstressed concrete. During the initial phases of the corrosion, compressive stresses at levels of 15 %, 20 %, and 25 % enhance the concrete's compressive strength by 2.8 %-10.1 %. However, this initial enhancement transitions to deterioration as external stress levels and corrosion time increase. SEM images validate these findings, showcasing initially denser internal structures in CSLC (15 %-25 %) compared to unstressed concrete (0 %), but severe deterioration at a 30 % stress level. Additionally, the strain-rate effect is more pronounced in unstressed concrete initially, with enhancement ranging from 12 % to 15 %, but gradually diminishes with increasing stress levels and corrosion time. It can be concluded that service stress significantly accelerates the long-term deterioration of concrete exposed to acid rain and should not be ignored in practical analysis.