Abstract:Mesoporous Y composites which exhibit both crystallized micropores and large mesopores with narrow mesopore diameter distributions and controlled pore diameters were successfully synthesized. The composite is synthesized through an elaborate design of the SiO2@cationic surfactant cetyltrimethylammonium bromide (SiO2@CTAB) micelle swelled by an appropriate amount of 1,3,5-trimenthylbenzene (TMB); it is subsequently fabricated from the condensing of the Y zeolite precursors, which contain Y zeolite seeds, on the mesoscale micelle followed by a hydrothermal crystallization process. The effect of synthesis conditions such as the amounts of CTAB, TMB and TEOS added to the synthesis system on the physicochemical properties of the obtained products was examined. The as-synthesized materials were carefully characterized by employing XRD, N-2 adsorption-desorption, SEM, TEM and pyridine-adsorbed FTIR techniques. The mesoporous Y zeolite exhibited both the typical diffraction characteristics of Y zeolites in the wide-angle XRD pattern, and the typical diffraction characteristics of a narrowly dispersed mesopore structure in the small-angle XRD pattern is successfully synthesized for the first time. Finally, the adsorption capacity for DBT and 4,6-DMDBT by samples with different mesopore diameters were assessed by a batch method. Sample MY-0.5C-0.35T-0.9B showed the highest capacity for adsorbing DBT in model diesel, and sample MY-0.5C-0.35T-1.5B showed the highest capacity for adsorbing 4,6-DMDBT in model diesel. Most importantly, sample MY-0.5C-0.35T-1.5B showed the highest adsorptive rate for both DBT and 4,6-DMDBT, which is at least 10 times faster than that of sample MY-0C-0.35T-0B because of the elimination of the diffusion limitation.

Highly Acidic Mesoporous Aluminosilicates Prepared from Preformed HY Zeolite in Na2SiO3 Alkaline Buffer System

Highly acidic mesoporous aluminosilicates assembled from zeolitic subunits generated by controllable desilication of ZSM-5 in Na2SiO3 solution

Continuous Synthesis of Mesoporous Y Zeolites from Normal Inorganic Aluminosilicates and Their High Adsorption Capacity for Dibenzothiophene (DBT) and 4,6-Dimethyldibenzothiophene (4,6-DMDBT)

Synthesis, Characterization, and Catalytic Properties of Stable Mesoporous Aluminosilicates Assembled from Preformed Zeolite L Precursors

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

High-Surface-Area Zeolitic Silica with Mesoporosity

Synthesis of Mesoporous Molecular Sieves with Secondary Building Units of Y Zeolite by Using Surfactants in Low Concentration as Template

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity

Mesoporous Zeolitic Materials (MZMs) Derived From Zeolite Y Using a Microwave Method for Catalysis

Understanding of the High Hydrothermal Stability of the Mesoporous Materials Prepared by the Assembly of Triblock Copolymer with Preformed Zeolite Precursors in Acidic Media

Synthesis of mesoporous high-silica zeolite Y and their catalytic cracking performance

Synthesis and Catalytic Performances of Mesoporous Aluminosilicates of Cubic and Hexagonal Structure with Stronger Acid Sites

Hydrothermal Synthesis of MCM-41-HY Mesoporous and Microporous Zeolite

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Synthesis of Mesoporous Materials with High Hydrothermal Stability from Mcm-22

Highly Efficient Synthesis of Zeolite Mcm-22 under Static Hydrothermal Crystallization Conditions

High-Temperature Synthesis of Zeolite Y

Sequential Microwave-Assisted Dealumination and Hydrothermal Alkaline Treatments of Y Zeolite for Preparing Hierarchical Mesoporous Zeolite Catalysts

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

Synthesis and structural properties of hierarchically structured aluminosilicates with zeolite y (FAU) frameworks