Microstructure and Mechanical Properties of Sintered and Forged Fe-2Cu-0.5C-0.11S Materials
YANG Shuo,XIAO Zhi-yu,GUAN Hang-jian,ZHANG Wen,WEN Li-ping
DOI: https://doi.org/10.3969/j.issn.1001-3784.2017.01.004
2017-01-01
Abstract:Sintered and forged Fe-2Cu-0.5C-0.11S materials were prepared from domestic raw materials.Density,microstructure,static mechanical properties,and dynamic ultrasonic fatigue property of the materials were investigated.The results show that forging can effectively improve the density of the parts.An average density of 7.75 g/crm3 (relative density of 98.7％) is obtained.The microstructures of the sintered and forged samples are mainly composed of pearlite and ferrite,but the porosity of the forged samples is obviously less.The mechanical properties of the forged samples are improved significantly compared with those of the sintered samples.The tensile strength,yield strength,elongation,and hardness of the forged samples are 1018 MPa,778 MPa,4.0％,and HB 206,respectively,which increases by 155％,145％,167％,and 87％ than those of the sintered samples.Ultrasonic fatigue strength of the forged samples for 106,107,and 108 weeks is 437.7 MPa,351.1 MPa,and 281.7 MPa,respectively,which increases by 82％,70％,and 59％ than those of the sintered samples.In the same fatigue life,the fatigue strength of the forged samples is higher than that of the sintered samples,but the differences decrease with the increase of fatigue life.The sintered and forged samples all show the characteristics of brittle fracture in general,and the microscopic plastic deformation exists both in the sintered and forged samples.