Abstract:The high chromium cast irons (HCCIs) with rare earth (RE) nanoparticles or inoculants were fabricated in the casting process. The phase compositions and microstructure were analyzed by X-ray diffraction (XRD) and optical microscopy (OM), respectively. The hardness and impact toughness were tested by Rockwel-hardmeter and impacting test enginery. And then, the morphology of fracture was researched by scanning electron microscopy (SEM). The results demonstrated that the phase compositions of HCCIs with addition of RE nanoparticles or inoculants which were M7C3 carbides + alpha-Fe did not change obviously. However, the prime M7C3 carbides morphology had great changes with the increase of RE nanoparticles, which changed from long lath to granular or island shape. When the content of RE nanoparticles was 0.4 wt.%, the microstructure of high chromium cast iron was refined greatly. The microstructure of carbides was coarser when the addition of RE nanoparticles was higher than 0.4 wt.%. The hardness and impact toughness of HCCIs were improved by addition of RE nanoparticles or inoculants. The impact toughness of HCCIs was increased 36.4% with RE nanoparticles of 0.4 wt.%, but the hardness changed slightly. In addition, the adding of RE nanoparticles or inoculants could reduce the degree of the brittle fracture. Fracture never seemed regular, instead, containing lots of laminates and dimples with the increase of the RE nanoparticles. The results also indicated that the optimal addition amount of the RE nanoparticles was 0.4%, under this composition, the microstructure and mechanical property achieved the best cooperation. In addition, through the study of erosion wear rate, when adding 0.4% RE nanoparticles into the HCCIs, the erosion wear rate got the minimum 0.32x10(-3) g/mm(2), which could increase 51.5% compared with that without any RE nanoparticles.

The Effect of Nano-Additives Containing Rare Earth Oxides on Sliding Wear Behavior of High Chromium Cast Iron Hardfacing Alloys

Effect of Submicron SiC Particles on the Properties of Alcocrfeni High Entropy Alloy Coatings

Effect of Process Parameters on Microstructure and Properties of AlCoCrFeNi-WC-WS2 Composite Coating Prepared by Laser Cladding

Effect of Nano-Additives on Microstructure, Mechanical Properties and Wear Behaviour of Fe⿿Cr⿿B Hardfacing Alloy

Effect of rare earth oxide nano-additives on micro-mechanical properties and erosion behavior of Fe-Cr-C-B hardfacing alloys

Study of Work Function and Dry Sliding Wear Behavior of Fe-Based Hardfacing Alloys with and Without Nano Rare Earth Oxides

Sliding wear behavior of Cr–Mo–Cu alloy cast irons with and without nano-additives

Dry sliding wear behavior of Fe-Cr-C-B hardfacing alloy modified with nano-CeO2 and its mechanisms of modification

Research on Wear Performance of Nano-Additives Cr-Mo-Cu Alloy Cast Iron

Effect of Rare Earth Oxide Nano-Additives on the Corrosion Behavior of Fe-based Hardfacing Alloys in Acid, Near-Neutral and Alkaline 3.5 Wt.% NaCl Solutions

Bending Strength and Wear Behavior of Fe-Cr-C-B Hardfacing Alloys with and Without Rare Earth Oxide Nanoparticles

Effect of Chromium on Microstructure and Wear Resistance of Fe-Cr-C Hardfacing Alloys

Effect of Nano-Y2O3 on the Microstructure and Properties of Fe-Cr-C-N-Al Surfacing Alloy

Effect of cooling conditions on microstructure evolution and wear behavior of high chromium cast iron hardfacing layer

Investigation of Stress Field and Wear Depth of Cr-Mo-Cu Alloy Cast Iron with Nano-Additives under Abrasive Wear

Effect of C additions to the microstructure and wear behaviour of CoCrFeNi high-entropy alloy

Influence of Rare Earth Nanoparticles and Inoculants on Performance and Microstructure of High Chromium Cast Iron

Influence of Al Addition on the Microstructure and Wear Behavior of Laser Cladding FeCoCrNiAlx High-Entropy Alloy Coatings

Effect of Chromium Content on Microstructure, Hardness, and Wear Resistance of As-Cast Fe-Cr-B Alloy

Effect of alloying elements on microstructure, wear, and corrosion behavior of Fe-based hardfacing

Effects of Al Addition on Microstructure and Wear Properties of AlxFeCrCoCuV High-entropy Alloys