Abstract:Arrays of well-aligned ZnO nanorods have been grown on Si substrates at 600 degrees C using a catalyst-free pulsed laser deposition (PLD) method, with and Without pre-deposition of a thin ZnO layer at a lower substrate temperature. Deposited products were analyzed and characterized by scanning and transmission electron microscopy (SEM and TEM), energy dispersive X-ray analysis, X-ray diffraction and photoluminescence (PL) measurements. EM revealed that rods grown directly on Si exhibit needle-like morphologies, with diameters, d, typically in the range 20-60 nm, lengths similar to 200-800 nm and, in most cases, capping particles of similar cross-section at their tips. HRTEM images show that these nanoparticles are ZnO also, suggesting that these derive from post-growth crystallisation of oxygen rich molten zinc droplets that cap the nanorods during growth. PLD of ZnO onto Si substrates that have been pre-coated with a thin ZnO film deposited at 300 degrees C yields denser, more uniform arrays of longer (similar to 1-1.2 mu m), thinner (d similar to 6-20 nm) nanorods, without any obvious capping particle. This suggests that a ZnO buffer layer can play a useful role in providing a high density of nucleation sites for subsequent growth of smaller diameter nanorods. The respective product arrays are most readily understood in terms of vapor-liquid-solid (V-L-S) and vapor-solid (V-S) growth models, respectively. Comparative studies of the room temperature PL from the respective samples reveal much higher UV emission intensity from nanorod arrays grown on the ZnO pre-coated Si substrates. (C) 2005 Elsevier Ltd. All rights reserved.

Growth of aligned ZnO nanorod arrays by catalyst-free pulsed laser deposition methods

Growth Mechanisms for ZnO Nanorods Formed by Pulsed Laser Deposition

Growth of Well-Aligned ZnO Nanorod Arrays on Si Substrates by Thermal Evaporation of Cu-Zn Alloy Powders.

Catalyst-free Synthesis of ZnO Nanorod Arrays on InP (001) Substrate by Pulsed Laser Deposition

Controllable Growth of Well-Aligned Zno Nanorod Arrays by Low-Temperature Wet Chemical Bath Deposition Method

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Selective Growth of Vertical-aligned ZnO Nanorod Arrays on Si Substrate by Catalyst-free Thermal Evaporation

MgxZn1-xO Nanorod Arrays Synthesized by Pulsed-Laser Deposition

Growth Mechanism And Properties Of Zno Nanorods Synthesized By Plasma-Enhanced Chemical Vapor Deposition

Self-Catalyst Synthesis of Aligned Zno Nanorods by Pulsed Laser Deposition

Well-Aligned Zno Nanocolumns Grown by Reactive Electron Beam Evaporation

Catalyst-Free Growth and Optical Properties of Vertically Aligned ZnO Nanorod Arrays on Si Substrates Covered with Thin Buffer Layers

Aligned Growth of ZnO Nanowires by Laser Ablation and Their Applications

Controlled Growth of ZnO Nanowires by Nanoparticle-Assisted Laser Ablation Deposition

Synthesis and Optical Properties of Well-Aligned ZnO Nanorod Array on an Undoped ZnO Film

Synthesis, microstructure and photoluminescence of well-aligned ZnO nanorods on Si substrate

Photoluminescence and Lasing Properties of Catalyst-Free ZnO Nanorod Arrays Fabricated by Pulsed Laser Deposition

Aligned ZnO Nanorod Arrays Fabricated on Si Substrate by Solution Deposition

Controllable Synthesis of Vertically Aligned ZnO Nanorod Arrays in Aqueous Solution.

Growth of vertically aligned ZnO nanorods using textured ZnO films

Growth of Vertically Aligned ZnO Nanowire Arrays on ZnO Single Crystals