Abstract:ZnO seed layers were deposited on silicon substrates by the pulsed laser deposition (PLD) method. ZnO nanorod arrays with different orientation degrees were grown using the chemical vapor deposition (CVD) method, and their field emission (FE) properties were studied. The ZnO seed layer with a thickness of approximately 450 nm exhibits a high c-axis orientation and possesses few defects. ZnO nanorods with similar lengths of approximately 22 mu m grow along the [0001] direction and contain a large number of oxygen vacancy defects. ZnO nanorods with a high orientation have the varying diameters from 160 to 230 nm and the areal density of approximately 2.6 x 10(8)/cm(2), while those with random orientation have a uniform diameter of approximately 130 nm and the areal density of approximately 5 x 10(7)/cm(2). The turn-on electrical field for the ZnO nanorod array with high orientation was 9.2 V/mu m, and the field enhancement factor was 1225, while that for the ZnO nanorod array with random orientation was 7.1 V/mu m, and the field enhancement factor was 1406. The better FE brightness distribution uniformity and the FE current density stability were obtained. The effect factors on the FE property have been discussed.

MgxZn1-xO Nanorod Arrays Synthesized by Pulsed-Laser Deposition

ZnMgO Nanorod Arrays Grown by Metal-Organic Chemical Vapor Deposition

Rod-Like Zinc Oxide Constructed by Nanoparticles: Synthesis, Characterization and Optical Properties

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Phosphorus Doped Zn(1-x)Mg(x)O Nanowire Arrays.

Photoluminescence and Lasing Properties of Catalyst-Free ZnO Nanorod Arrays Fabricated by Pulsed Laser Deposition

Quasi-aligned Zn1−xMgxO Nanorods Synthesized by Thermal Evaporation

Fabrication of ZnO Nanorods by Pulsed Nd:YAG Laser Ablation Deposition

Aligned ZnO Nanorod Arrays Fabricated on Si Substrate by Solution Deposition

Synthesis and Optical Properties of Well-Aligned ZnO Nanorod Array on an Undoped ZnO Film

Photoluminescence and Low-Threshold Lasing of ZnO Nanorod Arrays.

Synthesis of Zno/Cubic (zn, Mg)O Heterostructure Nanorods

Heteroepitaxial Growth of ZnO Nanorod Arrays on GaAs (111) Substrates by Electrochemical Deposition

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Structural and Optical Properties of Single Crystal Zn1-Xmgxo Nanorods - Experimental and Theoretical Studies

Preparation and Photoluminescence Properties of ZnO Nanowire/Nanorod Mix Arrays

Growth and Formation Mechanism of C-Oriented ZnO Nanorod Arrays Deposited on Glass

Fabrication and Field Emission Properties of ZnO Nanorod Arrays with Different Orientation Degrees

Synthesis and Characterization of Quasi-Aligned Zncdo Nanorods

Photoluminescence Characterization of Nanocrystalline ZnO Array

Chemical Growth of Zno Nanorod Arrays on Textured Nanoparticle Nanoribbons and Its Second-Harmonic Generation Performance