Preparation and Properties of Polypropylene/Graphite Composites with High Thermal Conductivity
Jiawei Wu,Xinyu Ji,Jindi Yang,Rongrong Qi,Xinwei Wang,Ping Wang,Xiangyang Wu
DOI: https://doi.org/10.3969/j.issn.1001-3539.2016.08.008
2016-01-01
Abstract:In order to improve the thermal conductivity of polypropylene (PP) and expand its applications,low cost com-mercial graphite was used to modify PP and the PP/graphite composites were prepared by using Haake torque rheometer. The ef-fects of graphitefillers with particle size of 2μm and 20μm and their compound on the thermal conductivity and mechanical properties were researched. The results show that increasing graphite content can apparently increase the thermal conductivity of the composites and the composites with 20μm graphite have a higher thermal conductivity. Due to anisotropy of graphite,the in-plane thermal conductivity is apparently higher than the through-plane thermal conductivity. Additionally,mixing the two graphite fillers,controlling the total mass fraction of thefillers to 40%,when the mass ratio of the 2μm graphite and 20μm graphite is 1︰5,the through-plane and in-plane thermal conductivity value reach peak and they are 1.125 W/(m·K) and 2.897 W/(m·K), respectively,which increases by 121%,61% than the compositefilled with 2μm graphite and by 3.6%,20% than the composite filled with 20μm graphite under same contents. When the graphite content increases,the tensile and bending strength of the compositesfilled by graphite with single particle size tend to declinefirstly and then increase,and with the increase of the content of 20μm graphite in the two graphitefillers compound,the mechanical properties of the composites decrease,but the bending strength decreases slightly and the tensile strength is also above 10 MPa.