An Experimental Study on Catalytic Aquathermolysis of Shanjiasi Heavy Oil
WANG Jie-Xiang,FAN Ze-Xia,REN Shang,WANG Lan-Lan,YAN Fang-Ping
2006-01-01
Abstract:The catalystic efficiency(CE) of a commercial water soluble Mo salt catalyst,A,and a specially prepared oil soluble Mo salt catalyst,B,is investigated for aquathermolysis(Ath) of heavy crude oil(HCO) of Shanjiasi,Shengli;the HCO is of viscosity of 50℃ 111.469 Pa·s and contains 0.42% surfur(S),46.5% resin(R),16.5% asphaltene(As) with H/C=1.68.Under conditions of 10% water charge(WC),Ath temperature 260℃ and ATh time 24 hrs,the viscosity reduction rate(VRR) for aquathermolyzed HCO keeps high values at dosage of 0.05—0.15% B,reaching a maximal value at dosage of 0.08% B,and has a notable peak value at dosage of 0.2% A;the CE of 0.08% B is much better than that of 0.2% A: the VVR,the S,R,and As contents,and the H/C ratio obtained are of 71.2% and 62.3%,0.23% and 0.29%,26.3% and 32.6%,10.3% and 11.4%,and 1.7 and 1.69 for 0.08% B and 0.2% A used,respectively.The CE of 0.2% A increases with increasing WC and reaches optimum at WC=20%,at which the VRR and the R and As contents of aquathermolyzed HCO is of 65.8%,27.2%,and 10.6%,respectively;the CE of 0.08% B is poor at WC=5% and is satisfactory and practically stable at WC=10—50%.The curves of As content and VRR vz ATh time show that the ATh rate and extent with 0.08% B increase with increasing ATh temperature at the initial stage and approximate to an equilibrium with a VRR being of 72% at 280℃ in 12 hrs,64% at 240℃ in 24 hrs, and 20% at 180℃ in 24 hrs.Oil soluble Mo salts are prior to water soluble ones when used as catalyst for ATh of HCOs.