Abstract:A modified nano-calcium carbonate (R-CCR) was prepared by coating a layer of unsaturated hydroxylfatty acid on the surface of CCR powders using a solid state method; the latter were commercial nano-CaCO 3 modified with stearic acid. FTIR studies indicate that the modifier is combined on the surface of CaCO 3 . PP/EPDM/nano-CaCO 3 ternary composites were prepared by a melt-mixing method. SEM and TEM were utilized to examine the morphology of the composites. The tensile fractured surface of PP/EPDM/R-CCR showed a fibroid morphology and large-scale yield deformation. The impact fractured surface showed that the amount of cavities in the PP/EPDM/R-CCR system was increased, however their size diminished obviously. R-CCR particles were dispersed uniformly in the PP matrix, and their compatibility was distinctly improved as compared to CCR when the amount of R-CCR was 15 h −1 . The tensile strength remained nearly constant (reduced from 27.6 MPa to 27.5 MPa), while the impact strength increased from 9.6 kJ/m 2 to 15.4 kJ/m 2 as CCR was replaced by R-CCR. Meanwhile, the bending strength and bending modulus also increased correspondingly. Furthermore, the impact strength of PP/EPDM/R-CCR was maintained at a high level (15.4 kJ/m 2 ), which was more than the sum of that of PP/EPDM and PP/R-CCR (6.6 kJ/m 2 and 6.1 kJ/m 2 respectively). This indicates that the R-CCR and EPDM have a significant synergistic toughening effect on PP while maintaining the strength and modulus of virgin PP. Both the storage modulus G′ and loss modulus G″ of PP/EPDM and PP/EPDM/R-CCR composites increase with increasing frequency, but the values of G′ and G″ of the tertiary composite are relatively higher than those of the binary system. The loss factor and viscosity decrease with increasing frequency, but there is little difference between tertiary and binary composites. The apparent viscosity η of the tertiary system containing R-CCR is lower than that of the tertiary system containing CCR and virgin PP. The viscosity of the composites sig-nificantly decreases with increasing shear rate. The mea-sured mechanical properties of the composites indicate that replacing CCR with R-CCR for binary composites could simultaneously enhance the toughness and strength of PP.

Morphology and properties of PP/EPDM/nano-CaCO3 composite

Morphology and Properties of PP/EPDM Binary Blends and PP/EPDM/nano‐CaCO3 Ternary Blends

The Morphology and Mechanical Properties of PP/EPDM/nano-CaCO3 Composites: Effect of Initial Mixing State

The Effects of Different Processing Methods on the Morphology and Properties of PP/EPDM/Nano-CaCO3 Ternary Blend

Crystallization Kinetics for PP/EPDM/Nano-CaCO3 Composites – the Influence of Nanoparticles Distribution

Study on Properties of PP/nano-CaCO_3/POE Composite

Study on the Properties and Structure of Polypropylene Modified with Nano-Sized CaCO_3

Crystallization Behavior of PP in Composites with EPDM and a Surface Modified Nano-Calcium Carbonate

Morphology and mechanical properties of PP/POE/nano‐CaCO3 composites

Mechanical and Thermal Properties of Polypropylene (PP) Composites Filled with CaCO3 and Shell Waste Derived Bio-Fillers

The Cellular Structure and Mechanical Properties of Polypropylene/Nano-CaCO3/Ethylene-propylene-diene-monomer Composites Prepared by an In-Mold-Decoration/Microcellular-Injection-Molding Process

Effect of Nano-CaCO3 on Properties of EPDM/Polypropylene Thermoplastic Vulcanizate

Investigations on Nano-CaCO3 Reinforced and Toughening Polypropylene/Elastomer Composites

Phase Structure and Mechanical Properties of Ternary Polypropylene/Elastomer/Nano-Caco3 Composites

Effect of Flow Fields on Morphology of Pp/Nano-Caco3 Composite and Its Rheological Behavior

Crystallization and melting behavior of nano-CaCO3/polypropylene composites modified by acrylic acid

Morphologies and Properties of PLA/PBAT/nano-CaCO3 Ternary Composite

Morphology Prediction of Ternary Polypropylene Composites Containing Elastomer and Calcium Carbonate Nanoparticles Filler

Effect of Unsaturated Hydroxyl-Fatty Acid Modified Nano-Caco3 on the Morphological and Rheological Behavior of PP

Effect of Dispersion Condition of Calcium Carbonate on the Crystallization and Melting Behavior of Polypropylene/CaCO3Nanocomposites

Mechanical Properties Of Pp/Epdm/Nano-Sio2 Ternary Composites