Abstract:Abstract Zn-Ni ferrite nanoparticles were successfully synthesized by coprecipitation method. The samples were annealed at various temperatures, i.e., 200 °C, 400 °C, 600 °C, 800 °C, and 1000 °C. The nanoparticles have the mixed spinel phase structure as confirmed by the X-ray diffraction patterns. The crystallite size was 15.1 nm and increased to 25.1 nm after annealing at 1000 °C. Transmission electron microscope images showed that the annealed sample exhibited better dispersion and grain boundaries compared to the as-prepared sample. Fourier transform infra-red spectra showed the existence of vibrations at 378 cm −1 and 555 cm −1 , confirming bonding for mixed spinel ferrites. The hysteresis measurement by using vibrating sample magnetometer confirmed that the sample possessed soft magnetic properties with a coercivity of 45 Oe and increased after annealing. The saturation magnetization of the as-prepared sample was 11 emu g −1 , and increased to 58 emu g −1 after annealing at a temperature of 800 and 1000 °C. The specific absorption rate (SAR) with an alternating current magnetic field (50 Hz and 100 Oe) of Zn-Ni ferrite before and after annealing (at 800 °C) was 63.7 and 92.4 mW g −1 , respectively. The results showed that annealing temperature has a significant role in determining the microstructural, the magnetic properties and the SAR of the nanoparticles.

Effect of annealing on the optical absorption of Ni nanoparticles in MgO single crystals

Annealing Effects on the Microstructure and Photoluminescence Properties of Ni-Doped Zno Films

Study on Surface Morphology and Optical Absorption Properties of Ni Ions Implanting SiO2

Optical Properties and Structure Characterization of Sapphire after Ni Ion Implantation and Annealing

Optical Properties of Metallic Nanoparticles in Ni-ion-implanted Α-Al2o3 Single Crystals

The effect of annealing atmosphere on structure characteristics of magnesium diffused lithium niobate single crystal substrates

Effects Of Annealing On Optical Properties Of Zn-Implanted Zno Thin Films

Effect of Annealing Temperature on the Optical and Electrical Properties of N Doped MgZnO Films

Effect of Annealing Conditions on the Structural, Electrical and Optical Properties of Li-doped NiO Thin Films

Magnetic nano-particles of Ni in MgO single crystals by ion implantation

Optical and Magnetic Properties of Ni/Nio Nanopartilces in Ysz by Metal Ion Implantation and Post-Implantation Annealing

Study of Optical Properties and TEM of Nanoparticles in Ni + -Implanted Sapphire

Formation of Optical Waveguide and Annealing Behaviour of LiNbO 3 Implanted by 3.0-Mev Nickel Ions

Influence of annealing on microstructure and defect-related photoluminescence of Ni0.7Zn0.3O thin film

The Effect of Ni Pre-Implantation on Surface Morphology and Optical Absorption Properties of Ag Nanoparticles Embedded in SiO2

Effect of annealing temperature on the optoelectronic properties and structure of NiO films

Annealing Effect on Properties of Zno Thin Films Grown on LiNbO3 Substrates by MOCVD

[Effects of Annealing Temperature on the Structure and Optical Properties of ZnMgO Films Prepared by Atom Layer Deposition].

Effect of annealing on optical properties of Mg(x)Zn(1-x)Othin films deposited at low temperature

Effects of annealing temperature on microstructural, magnetic properties, and specific absorption rate of Zn-Ni ferrite nanoparticles

The Annealing Behavior of Cu Nanoparticles in Ar-ion Implanted Spinel